Lei Wang

Graphene quantum dots (GQDs) with distinct optical responses were prepared from pyrene using urea, melamine, and 2,4-pyridinedicarboxylic acid as nitrogen-containing regulators and were subsequently combined with ZIF-8 for visible-light-driven CO₂ reduction. FT-IR, Raman, XRD, optical spectroscopy, representative high-magnification transmission electron microscopy, and X-ray photoelectron spectroscopy (XPS) showed regulator-dependent structural, compositional, and optical differences. XPS detected surface nitrogen in all three GQD samples, with the highest N content in y-GQDs, while the relative N 1s component distributions differed across the series. At a nominal 4 wt% GQD addition, r-GQDs/ZIF-8 gave the highest observed mean CO and CH₄ formation rates of 23.51 ± 0.48 and 4.08 ± 0.15 μmol·g⁻¹·h⁻¹, respectively, corresponding to approximately 2.9- and 4.5-fold increases over pristine ZIF-8. This sample also showed the lowest fitted charge-transfer resistance, the highest mean photocurrent density, and the fastest qualitative time-resolved photoluminescence decay among the compared composites. Across three independent five-cycle tests, 83.78 ± 0.54% of the initial combined CO and CH₄ rate was retained. These results establish correlations among regulator identity, surface composition, optical relaxation, photoelectrochemical response, and catalytic activity, but do not determine a unique charge-transfer pathway or exclude contributions from surface basicity, CO₂ adsorption, and nominal-loading differences.

Graphene quantum dots (GQDs) represent a class of promising nanomaterials characterized by adjustable optical properties, making them well suited for applications in biosensing and chemical detection. However, challenges persist in achieving scalable, cost-effective synthesis and enhancing detection sensitivity. In this study, we have developed a simple and environmentally friendly method to prepare blue graphene quantum dots, c-GQDs, using nitronaphthalene as a precursor, and yellow graphene quantum dots, y-GQDs, using nitronaphthalene doped acid. The quantum yield is 29.75%, and the average thickness is 2.08 nm and 3.95 nm, respectively. The synthesized c-GQDs exhibit a prominent cyan fluorescence at a wavelength of 490 nm under excitation at 380 nm, while the y-GQDs show a distinct yellow fluorescence at a wavelength of 540 nm under excitation at 494 nm. The introduction of p-aminobenzoic acid (PABA) introduced a marked red shift in fluorescence, attributed to the electron-withdrawing effect of the carboxyl groups on PABA. This key finding significantly enhanced the sensitivity of GQDs for detecting trace copper(II) ions (Cu²⁺), a heavy metal contaminant posing serious environmental risks. The fluorescence of the GQDs was selectively quenched in the presence of Cu²⁺, facilitating accurate and sensitive detection even in complex ion matrices. Mechanistic studies revealed that the quenching effect is driven by strong static quenching interactions, which inhibit non-radiative transitions. This work not only introduces a scalable method for producing high-performance GQDs but also highlights their potential as effective fluorescent probes for environmental monitoring and heavy metal ion detection.

Methyl orange (MO) is an organic synthetic dye widely used in laboratory and industrial applications. In laboratory settings, it serves as an acid–base indicator due to its distinct color change in both acidic and alkaline environments. Industrially, it is primarily utilized in the textile industry for its ultraviolet (UV) absorption properties. However, the discharge and leakage of methyl orange into the environment can cause severe ecological damage and pose potential carcinogenic and teratogenic risks to human health. Therefore, detecting and quantifying the concentration of methyl orange in various matrices is crucial. This study reports the synthesis of graphene quantum dots (GQDs) from orange peel as a precursor, using ethanol and dimethylformamide (DMF) as solvents. Cyan (c-GQDs) and yellow (y-GQDs) graphene quantum dots were synthesized through a bottom-up hydrothermal method. The difference in color is attributed to the redshift caused by the varying ratio of pyridine nitrogen to pyrrole nitrogen. These GQDs exhibited notable optical properties, with c-GQDs emitting cyan fluorescence and y-GQDs emitting yellow fluorescence under UV light. To investigate fluorescence quenching effects, nine commonly used dyes were tested, and all were found to quench the fluorescence of y-GQDs, with methyl orange having the most significant effect. The fluorescence quenching of orange peel-derived GQDs in the presence of methyl orange is attributed to poor dispersion in DMF solution. Additionally, the GQDs possess high specific surface area, abundant surface functional groups, and excellent electronic conductivity, which contribute to their effective fluorescence quenching performance. The average thickness of y-GQDs (the vertical dimension from the substrate upwards) was 3.51 nm, confirming their graphene-like structure. They emitted yellow fluorescence within the wavelength range of 450–530 nm. Notably, a significant linear correlation was found between the concentration of methyl orange and the fluorescence intensity of y-GQDs (regression coefficient = 0.9954), indicating the potential of GQDs as effective sensing materials for organic pollutant detection.

Lignin is a unique renewable aromatic resource in nature. In the past decades, researchers have attempted to breakdown the linkage bonds in lignin to provide aromatic platform chemicals that used to come from the petrochemical industry. In recent years, electrochemical lignin degradation under mild conditions has drawn much attention from the scientific community owing to its potential to scale up and its environmental friendliness. Sustainable electrochemical degradation of lignin consumes less energy and usually requires mild conditions, but low degradation efficiency and insufficient product selectivity are still significant challenges. The method for lignin degradation by reactive oxygen species (ROS) generated through the water oxidation reaction (WOR) at the anode and oxygen reduction reaction (ORR) at the cathode are more attractive for sustainable electrochemical degradation. The present contribution aims to review advancements in electrochemical degradation of lignin in aqueous or non-aqueous supporting electrolytes, focusing on the regulation of ROS in situ generated on the electrode.