Chang-Hee Cho
Current Organizations / Institutes
The organizations/institutes from the scholar's latest article
Research Subjects
Chang-Hee Cho has a total of 3 co-authors. Here are the top co-authors by number of shared publications:
- Dongearn Kim
Shape Manufacturing R&D Department, Korea Institute of Industrial Technology, Incheon 21999, Korea
1 shared publication - Hoon Cho
Korea Institute of Industrial Technology, Incheon 21999, Republic of Korea
1 shared publication - Je-Sik Shin
Korea Institute of Industrial Technology, KITECH, Incheon, Korea
1 shared publication
Latest Publications
- Open Access
Influence of Addition of Al and Ti Solutes and Variable Processing Conditions on Mechanical and Electrical Properties of Cu-Cr Alloys
To apply the electric component with high efficiency, the softening problem of material should be improved. Cu-Cr alloys are recognized to be proper materials to be applied. However, the softening problem has not been solved yet. In this study, the effect of Ti and Al on mechanical property and electrical conductivity in Cu-Cr alloy was investigated. Cr content is designed to up to 0.25 wt.% in order to be expected to improve electrical conductivity. During fabrication processing, microstructure identification, Cr concentration, lattice parameter, and micro-hardness in copper matrix were measured. Then, aging condition was investigated. Resistance about over-aging is increased compared to Cu-Cr and Cu-Cr-Al alloy added to Ti. The hardness and electrical conductivity are discussed by the working conditions and heat treatment, such as rolling, solid-solution treatment, and aging process, which improve the formability also at the optimum condition. Moreover, the role of Ti contents is studied. In the Cu-Cr alloys, the addition of both Al and Ti contents keeps the hardness from being reduced. As a result, the precipitation of Cr particles and the obstacle by Al and Ti contents to be softened are observed in this study.
Open AccessInfluence of Addition of Al and Ti Solutes and Variable Processing Conditions on Mechanical and Electrical Properties of Cu-Cr Alloys
To apply the electric component with high efficiency, the softening problem of material should be improved. Cu-Cr alloys are recognized to be proper materials to be applied. However, the softening problem has not been solved yet. In this study, the effect of Ti and Al on mechanical property and electrical conductivity in Cu-Cr alloy was investigated. Cr content is designed to up to 0.25 wt.% in order to be expected to improve electrical conductivity. During fabrication processing, microstructure identification, Cr concentration, lattice parameter, and micro-hardness in copper matrix were measured. Then, aging condition was investigated. Resistance about over-aging is increased compared to Cu-Cr and Cu-Cr-Al alloy added to Ti. The hardness and electrical conductivity are discussed by the working conditions and heat treatment, such as rolling, solid-solution treatment, and aging process, which improve the formability also at the optimum condition. Moreover, the role of Ti contents is studied. In the Cu-Cr alloys, the addition of both Al and Ti contents keeps the hardness from being reduced. As a result, the precipitation of Cr particles and the obstacle by Al and Ti contents to be softened are observed in this study.