Stearic acid and triethanolamine (TEA) in a molar ratio of 2:1 were mixed in aqueous solution at 80 °C and subsequently cooled to ambient temperature. The structural evolution of the resultant sample during storage was characterized by using light microscopy, Cryo-SEM, differential scanning calorimetery, pH, infrared spectroscopy, elemental analysis, and simultaneous small and wide-angle X-ray diffraction. It was found that a lamellar liquid crystalline phase was formed when stearic acid and TEA solution were mixed at 80 °C and multilamellar spheres of a few microns diameter were formed initially after cooling. A hydrolysis reaction (i.e., the reverse reaction of neutralization between stearic acid and TEA) occurred thereafter that caused the breakdown of the lamellar gel phase and the formation of platelet stearic acid crystals. Three polymorphs of stearic acid (defined following previous work as the A, C, and E forms) were formed as the result of hydrolysis reaction, which gave rise to a strong optically pearlescent appearance.

Crystals of partially neutralized stearic acid with triethanolamine (TEA) were prepared by mixing these two materials above 80 °C and then cooling. The crystalline composition and the structure and melting behavior of the resultant products were characterized with small-angle and wide-angle X-ray diffraction, thermal analysis, microscopy, and infrared spectroscopy. It was discovered that an acid−soap complex of 2:1 fixed stoichiometric ratio exists between stearic acid and TEA stearate. A binary phase diagram of stearic acid and TEA soap is built based on the experimental results; this is the first published record of a binary phase diagram for amine-based soap. Its behavior is significantly different from that of binary systems of fatty acid and alkali soap.