Madeline Van Winkle

The long-term stability of protonic ceramic electrolysis cell (PCEC) materials under high-steam operating conditions remains a critical barrier to device commercialization. Here, we investigate the fundamental degradation mechanisms of dense BaCe _0.7 Zr _0.1 Y _0.1 Yb _0.1 O _{3- δ} (BCZYYb) electrolytes operated at 550 °C, 50% H ₂ O in air. Over 1,000 h, the total electrolyte conductivity decreases by 11.1%, driven primarily by a >130% increase in grain-boundary resistivity. Post-mortem analyses reveal that damage is localized to near-surface grain boundaries extending ∼50 μ m into the dense electrolyte pellet. This surface localization indicates that degradation is likely to be severe in thin, device-level electrolytes. Degradation is primarily attributed to chemo-mechanical grain-boundary weakening arising from hydration-induced chemical expansion, culminating in the formation of intergranular cracks oriented parallel to the pellet surface. These internal cracks subsequently react with steam and/or CO ₂ , leading to the formation of nanoscale insulating phases, including Ba(OH) ₂ , nanocrystalline BaCO ₃ , and amorphous Ce/Zr/Y/Yb-containing oxides or hydroxycarbonates. After an initial degradation period of approximately 200 h, the overall conductivity stabilizes. Incorporating NiO sintering aids reduces grain-boundary density by an order of magnitude under identical sintering conditions. Although addition of NiO increases the initial resistivity by >160% at 550 °C, it substantially suppresses grain-boundary instability and mitigates chemical degradation. These findings underscore the urgent need for chemical and/or physical stabilization of BCZYYb electrolytes and offer design guidelines to enable durable, high-performance PCECs.

Thermal energy storage (TES) technology facilitates supply-demand energy management by storing heat in concentrated solar power, waste heat recovery, baseload nuclear plants, and industrial applications. Magnesium chloride (MgCl2) is a promising salt-based phase change material candidate for TES applications due to its favorable thermo-physical properties. However, the highly corrosive nature of this chloride-based salt in the molten state presents challenges for the realization of efficient TES system utilizing this salt. This study evaluates the performance of 304L stainless steel (SS304L) as a structural alloy in contact with MgCl2 under thermal cycling conditions relevant for TES applications. We utilize a multi-modal approach, integrating synchrotron-based sub-micron X-ray fluorescence and electron microscopy, to investigate the microstructural evolution and elemental diffusion at the alloy-salt (SS304L-MgCl2) interface under short- and long-term thermal cycling conditions. The primary corrosion mechanisms are discussed, revealing a shift in the dominant corrosion process between short- and long-term exposure.

Metal oxides are promising materials for long-duration thermochemical energy storage. Efforts to characterize their reaction kinetics, conversion rate, and morphological evolution during thermochemical cycling have largely focused on bulk and microscale measurements. However, the design of nanostructured metal oxides could improve the reaction reversibility and kinetics, warranting the development of platforms to investigate how these materials behave at the nanoscale. Here, we demonstrate the use of correlative, time-resolved electron energy loss spectroscopy and imaging in an environmental transmission electron microscope for studying the thermochemical cyclability of cobalt oxide nanoparticles with high spatial and temporal resolution. The spectroscopic data reveal a striking decrease in reaction kinetics after the first cycle, resulting from sintering-driven nanostructural densification. Comparison between cycling in humid and dry air shows that atmospheric conditions can modulate reaction transition temperatures but have limited effects on sintering over multiple cycles, suggesting long-term durability will instead rely on synthetic and/or nanostructural modifications.

Bragg interferometry (BI) is an imaging technique based on four-dimensional scanning transmission electron microscopy (4D-STEM) wherein the intensities of select overlapping Bragg disks are fit or more qualitatively analyzed in the context of simple trigonometric equations to determine local stacking order. In 4D-STEM based approaches, the collection of full diffraction patterns at each real-space position of the scanning probe allows the use of precise virtual apertures much smaller and more variable in shape than those used in conventional dark field imaging such that even buried interfaces marginally twisted from other layers can be targeted. With a coarse-grained form of dark field ptychography, BI uses simple physically derived fitting functions to extract the average structure within the illumination region and is, therefore, viable over large fields of view. BI has shown a particular advantage for selectively investigating the interlayer stacking and associated moiré reconstruction of bilayer interfaces within complex multi-layered structures. This has enabled investigation of reconstruction and substrate effects in bilayers through encapsulating hexagonal boron nitride and of select bilayer interfaces within trilayer stacks. However, the technique can be improved to provide a greater spatial resolution and probe a wider range of twisted structures, for which current limitations on acquisition parameters can lead to large illumination regions and the computationally involved post-processing can fail. Here, we analyze these limitations and the computational processing in greater depth, presenting a few methods for improvement over previous works, discussing potential areas for further expansion, and illustrating the current capabilities of this approach for extracting moiré-scale strain.

In conventional ferroelectric materials, polarization is an intrinsic property limited by bulk crystallographic structure and symmetry. Recently, it has been demonstrated that polar order can also be accessed using inherently non-polar van der Waals materials through layer-by-layer assembly into heterostructures, wherein interfacial interactions can generate spontaneous, switchable polarization. Here we show that deliberate interlayer rotations in multilayer van der Waals heterostructures modulate both the spatial ordering and switching dynamics of polar domains. The engendered tunability is unparalleled in conventional bulk ferroelectrics or polar bilayers. By means of operando transmission electron microscopy we show how alterations of the relative rotations of three WSe₂ layers produce structural polytypes with distinct arrangements of polar domains with either a global or localized switching response. Furthermore, the presence of uniaxial strain generates structural anisotropy that yields a range of switching behaviours, coercivities and even tunable biased responses. We also provide evidence of mechanical coupling between the two interfaces of the trilayer, a key consideration for the control of switching dynamics in polar multilayer structures more broadly.

Moiré superlattices formed by twisting trilayers of graphene are a useful model for studying correlated electron behaviour and offer several advantages over their formative bilayer analogues, including a more diverse collection of correlated phases and more robust superconductivity. Spontaneous structural relaxation alters the behaviour of moiré superlattices considerably and has been suggested to play an important role in the relative stability of superconductivity in trilayers. Here we use an interferometric four-dimensional scanning transmission electron microscopy approach to directly probe the local graphene layer alignment over a wide range of trilayer graphene structures. Our results inform a thorough understanding of how reconstruction modulates the local lattice symmetries crucial for establishing correlated phases in twisted graphene trilayers, evincing a relaxed structure that is markedly different from that proposed previously.

Lattice reconstruction and corresponding strain accumulation plays a key role in defining the electronic structure of two-dimensional moiré superlattices, including those of transition metal dichalcogenides (TMDs). Imaging of TMD moirés has so far provided a qualitative understanding of this relaxation process in terms of interlayer stacking energy, while models of the underlying deformation mechanisms have relied on simulations. Here, we use interferometric four-dimensional scanning transmission electron microscopy to quantitatively map the mechanical deformations through which reconstruction occurs in small-angle twisted bilayer MoS₂ and WSe₂/MoS₂ heterobilayers. We provide direct evidence that local rotations govern relaxation for twisted homobilayers, while local dilations are prominent in heterobilayers possessing a sufficiently large lattice mismatch. Encapsulation of the moiré layers in hBN further localizes and enhances these in-plane reconstruction pathways by suppressing out-of-plane corrugation. We also find that extrinsic uniaxial heterostrain, which introduces a lattice constant difference in twisted homobilayers, leads to accumulation and redistribution of reconstruction strain, demonstrating another route to modify the moiré potential.

Two-dimensional (2D) magnetic crystals hold promise for miniaturized and ultralow power electronic devices that exploit spin manipulation. In these materials, large, controllable magnetocrystalline anisotropy (MCA) is a prerequisite for the stabilization and manipulation of long-range magnetic order. In known 2D magnetic crystals, relatively weak MCA typically results in soft ferromagnetism. Here, we demonstrate that ferromagnetic order persists down to the thinnest limit of Fe_xTaS₂ (Fe-intercalated bilayer 2H-TaS₂) with giant coercivities up to 3 T. We prepare Fe-intercalated TaS₂ by chemical intercalation of van der Waals-layered 2H-TaS₂ crystals and perform variable-temperature transport, transmission electron microscopy, and confocal Raman spectroscopy measurements to shed new light on the coupled effects of dimensionality, degree of intercalation, and intercalant order/disorder on the hard ferromagnetic behavior of Fe_xTaS₂. More generally, we show that chemical intercalation gives access to a rich synthetic parameter space for low-dimensional magnets, in which magnetic properties can be tailored by the choice of the host material and intercalant identity/amount, in addition to the manifold distinctive degrees of freedom available in atomically thin, van der Waals crystals.