Andrew Claypole

The application of biodegradable polymeric coatings is an effective strategy to enhance the functional performance of paper-based materials while preserving their recyclability.This study investigates the relationship between polymer concentration, processability and performance of an ethylene-modified poly(vinyl alcohol) (m-PVOH) coating applied to a Kraft paper (KP) substrate.The rheology of aqueous m-PVOH solutions (5–30 wt%) were measured to assess their suitability for high-speed coating processes such as gravure and flexography, and the effect of ageing on their stability. Viscosity increased with polymer concentration, with a critical transition between 20 and 30 wt% where polymer–polymer interactions and irreversible structural rearrangements became dominant.Formulations containing 10–20 wt% m-PVOH were selected for paper coating based on the rheology and processability criteria. Higher polymer concentrations reduced impregnation into the paper matrix, leading to the formation of compact and continuous coating layers. The coated papers exhibited significantly enhanced air and water resistance, while maintaining stable oxygen and water vapour barrier properties (OTR ≈ 580 cm³/(m²·day·bar), WVTR ≈ 4 g/(m²·day)). The coatings also increased surface polarity and preserved the mechanical integrity of the substrate. m-PVOH formulations can enable scalable, recyclable, and environmentally friendly paper-based packaging solutions.

Inkjet printing inks are typically limited to low viscosities, employing highly dilute inks with low pigment loading compared with inks for other printing processes. This reduces color intensity, limits productivity, and requires higher drying energy. This study compares standard-viscosity graphic inkjet inks (~13 mPa.s shear viscosity) with higher-viscosity inkjet inks (~60 mPa.s), traditionally considered outside the normal jetting range, for print outcomes on corrugated cardboard with both white coated and brown uncoated liners. Higher-viscosity inks imparted greater color density to the print; this was assessed as being due to both the inherently higher viscosity of the ink reducing penetration into the substrate and the higher pigment loading capable of being contained within these inks. While standard-viscosity inks tended to plateau in color intensity as ink coverage was increased, higher-viscosity inks could increase in intensity throughout the entire coverage range on coated white liner. This effect was dependent on the substrate, with the coated white liner exhibiting up to a 67% increase in maximum color density but the uncoated brown liner showing up to a 13% increase. It is envisaged that wider adoption of higher-viscosity inks can increase both color intensity and printing speed, thus making inkjet more competitive with conventional printing processes.

The ability to maintain body temperature has been shown to bring about improvements in sporting performance. However, current solutions are limited with regards to flexibility, heating uniformity and robustness. An innovative screen-printed Nanocarbon heater is demonstrated which is robust to bending, folding, tensile extensions of up to 20% and machine washing. This combination of ink and substrate enables the heated garments to safely flex without impeding the wearer. It is capable of producing uniform heating over a 15 × 4 cm area using a conductive ink based on a blend of Graphite Nanoplatelets and Carbon Black. This can be attributed to the low roughness of the conductive carbon coating, the uniform distribution and good interconnection of the carbon particles. The heaters have a low thermal inertia, producing a rapid temperature response at low voltages, reaching equilibrium temperatures within 120 s of being switched on. The heaters reached the 40 °C required for wearable heating applications within 20 s at 12 Volts. Screen printing was demonstrated to be an effective method of controlling the printed layer thickness with good interlayer adhesion and contact for multiple printed layers. This can be used to regulate their electrical properties and hence adjust the heater performance.

For wearable electronic devices to be fully integrated into garments, without restricting or impeding movement, requires flexible and stretchable inks and coatings, which must have consistent performance and recover from mechanical strain. Combining Carbon Black (CB) and ammonia plasma functionalized Graphite Nanoplatelets (GNPs) in a Thermoplastic Polyurethane (TPU) resin created a conductive ink that could stretch to substrate failure (>300% nominal strain) and cyclic strains of up to 100% while maintaining an electrical network. This highly stretchable, conductive screen-printable ink was developed using relatively low-cost carbon materials and scalable processes making it a candidate for future wearable developments. The electromechanical performance of the carbon ink for wearable technology is compared to a screen-printable silver as a control. After initial plastic deformation and the alignment of the nano carbons in the matrix, the electrical performance was consistent under cycling to 100% nominal strain. Although the GNP flakes are pulled further apart a consistent, but less conductive path remains through the CB/TPU matrix. In contrast to the nano carbon ink, a more conductive ink made using silver flakes lost conductivity at 166% nominal strain falling short of the substrate failure strain. This was attributed to the failure of direct contact between the silver flakes.