Corinne Binet

This study examines the chemical, thermal, and dielectric properties of gel polymer electrolytes (GPEs) based on poly(ethylene glycol) diacrylate (PEGDA, average Mn=700 g/mol). GPEs were synthesized via a single-step UV-irradiation process, whereby PEGDA was mixed with varying concentrations of a commercial liquid electrolyte (1 M LiPF6 in EC/DEC 50/50 v/v) ranging from 0 to 60 wt%. The results of the infrared analysis indicated that the liquid electrolyte was successfully immobilized within the polymeric matrix. The thermally stable nature of the synthesized GPEs was confirmed across a wide temperature range (-40 to 90°C) through thermal analysis. Furthermore, dielectric measurements were conducted in a frequency range of 0.1 to 106 Hz, with a sinusoidal AC amplitude of 10 mV, from 20 to 100°C. The results demonstrated that the ionic conductivity of GPEs increased with the addition of liquid electrolyte. The GPEs prepared with 60 wt% liquid electrolyte exhibited a conductivity value of approximately 6.6x10-3 S/m at 30°C, which is consistent with the conductivity range reported in the literature.

Chemical, structural, and thermal properties of recovered nematic Liquid Crystal (LC) mixtures were investigated by applying several analytical techniques. A large quantity (65,700) of End-Of-Life (EOL) Liquid Crystal Display (LCD) screens were used to extract these LC blends. The studied EOL-LCD screens were heterogeneous in nature, particularly due to their different brands, production years, and dimensions. The collected TV and computer screens, as well as tablets, presented an average diagonal size of 24 inches. Chemical characterization revealed that the recovered compounds present typical chemical structures of LC molecules by the simultaneous presence of aliphatic chains and aromatic and polar groups. POM observations of these samples exhibited Schlieren and marble-like textures at room temperature, which are typical of nematic LCs. Moreover, thermal characterization and thermo-optical analysis showed that these LC mixtures displayed a broad nematic phase between −90 °C and +70 °C.

For several decades, Liquid Crystal Displays (LCDs) have been widely used in televisions, laptops, mobile phones, and other devices. Nowadays, liquid crystals (LCs) represent an important economic value of the recycling system of LCDs. The reuse of these organic molecules could become a profitable basis since it permits to preserve the value of these materials. In this context, the general objective of this work focuses on the recovery of LCs as well as on other valuable materials present in end-of-life LCDs. An orderly, manual LCD dismantling line is put into operation for differentiated recycling of electronic boards, cold cathode lamps that may contain mercury, polymers, metals, and other valuable materials. There is also an extraction line where LCD panels are opened and exposed to an ultrasonically activated organic solvent bath to recover LCs. The resulting solution contains LCs, solvent, organic and inorganic impurities. The LCs mixtures were purified and then characterized mainly by spectroscopic, chromatographic, and thermal techniques. A study of the influence of adding diamond nanoparticles at 0.05, 0.1 and 0.2 wt% to recycled LCs was also performed using dielectric spectroscopy. Dielectric properties of LCs were measured at room temperature, using an impedance analyzer in the frequency range from 0.1 to 10 6 Hz.

In the present work, the dielectric properties of recycled liquid crystals (LCs) (non-purified, purified, and doped with diamond nanoparticles at 0.05, 0.1, and 0.2 wt%) were investigated. The studied LC mixtures were obtained from industrial recycling of end-of-life LC displays presenting mainly nematic phases. Dielectric measurements were carried out at room temperature on a frequency range from 0.1 to 10⁶ Hz using an impedance analyzer. The amplitude of the oscillating voltage was fixed at 1 V using cells with homogeneous and homeotropic alignments. Results show that the dielectric anisotropy of all purified samples presents positive values and decreases after the addition of diamond nanoparticles to the LC mixtures. DC conductivity values were obtained by applying the universal law of dielectric response proposed by Jonscher. In addition, conductivity of the doped LC mixtures is lower than that of the undoped and non-purified LC.