Tattukolla Kiran

High-performance steel has emerged as an advanced structural material in the construction practice of industrial buildings, due to its excellent properties. However, fire poses a significant threat to cold-formed steel structures, as they are prone to deform and buckle under the exposure, potentially leading to building collapse. This study aimed to evaluate the post-fire web-crippling behaviour of high performance CFS sections for End Two Flange (ETF) and Interior Two Flange (ITF) load cases. Two types of specimens were used: CFS webs without holes and CFS webs with circular holes. All test specimens were heated according to the ISO 834 standard fire curve and were subsequently cooled by air or water. A total of 52 specimens (ambient and post-fire) were tested under ETF and ITF load conditions. The load-deflection behaviour and failure modes were evaluated through experimental and numerical analysis. Finite element modelling was used to compare the load-deflection behaviour and failure modes of CFS members with experimental results. The experimental results indicate that the web load-carrying capacity of the high-performance steel member decreases drastically as the heating duration increases. Furthermore, the ITF load case specimens exhibited a lower strength loss than the ETF load case specimens at elevated temperatures. There was an excellent agreement between the experimental and FEM results in terms of the load-carrying capacity and failure modes of high performance CFS.

The present research investigates the behaviour of sustainable Self-Compacting Concrete (SCC) when subjected to high temperatures, focusing on workability, post-fire impact resistance, and the effects of fire protection coatings. To develop environmentally friendly SCC mixes, Supplementary Cementitious Materials (SCM) such as Fly Ash (FA), Ground Granulated Blast Furnace Slag (GGBFS), and Expanded Perlite Aggregate (EPA) were used. Fifty-six cubes and ninety-six impact SCC specimens were cast and cured for testing. Fire-resistant Cement Perlite Plaster (CPP) coatings were applied to the protected specimens, a passive protection coating rarely studied. SCC (unprotected and protected) specimens, i.e., protected and unprotected samples, were heated following the ISO standard fire curve. An extensive comparative study has been conducted on utilising different SCMs for developing SCC. Workability behaviour, post-fire impact resistance, and the influence of fire protection coatings on sustainable SCC subjected to high temperatures are the significant parameters examined in the present research, including physical observations and failure patterns. The test results noted that after 30 min of exposure, the unprotected specimen exhibited a significant decrease in failure impact energy, ranging from 80% to 90%. Furthermore, as the heating duration increased, there was a gradual rise in the loss of failure impact energy. However, when considering the protected CPP specimens, it was observed that they effectively mitigated the loss of strength when subjected to elevated temperature. Therefore, the findings of this research may have practical implications for the construction industry and contribute to the development of sustainable and fire-resistant SCC materials.

Purpose: The construction industries at present are focusing on designing sustainable concrete with less carbon footprint. Considering this aspect, a Fibre-Reinforced Geopolymer Concrete (FGC) was developed with 8 and 10 molarities (M). At elevated temperatures, concrete experiences deterioration of its mechanical properties which is in some cases associated with spalling, leading to the building collapse.Design/methodology/approach: In this study, six geopolymer-based mix proportions are prepared with crimped steel fibre (SF), polypropylene fibre (PF), basalt fibre (BF), a hybrid mixture consisting of (SF + PF), a hybrid mixture with (SF + BF), and a reference specimen (without fibres). After temperature exposure, ultrasonic pulse velocity, physical characteristics of damaged concrete, loss of compressive strength (CS), split tensile strength (TS), and flexural strength (FS) of concrete are assessed. A polynomial relationship is developed between residual strength properties of concrete, and it showed a good agreement.Findings: The test results concluded that concrete with BF showed a lower loss in CS after 925 °C (i.e. 60 min of heating) temperature exposure. In the case of TS, and FS, the concrete with SF had lesser loss in strength. After 986 °C and 1029 °C exposure, concrete with the hybrid combination (SF + BF) showed lower strength deterioration in CS, TS, and FS as compared to concrete with PF and SF + PF. The rate of reduction in strength is similar to that of GC-BF in CS, GC-SF in TS and FS.Originality/value: Performance evaluation under fire exposure is necessary for FGC. In this study, we provided the mechanical behaviour and physical properties of SF, PF, and BF-based geopolymer concrete exposed to high temperatures, which were evaluated according to ISO standards. In addition, micro-structural behaviour and linear polynomials are observed.

Self-Compacting Concrete (SCC) is a special concrete that can flow easily across congested reinforcements. Also, it is easy to work with and does not segregate. The present investigation aims at the design and development of sustainable SCC with the employment of industrial by-products such as Fly Ash (FA), Ground Granulated Blast Furnace Slag (GGBFS), and Expanded Perlite Aggregate (EPA). Four SCC mixes were developed to attain a target strength of 30 MPa. Workability tests (slump flow, J-ring, and V-funnel tests) were performed following the EFNARC guidelines to ensure fresh SCC properties. Detailed experiments were conducted to evaluate the durability characteristics of the developed SCC, such as water absorption, sorptivity, acid attacks (sulphuric, nitric, sulphate, and chloride), the Rapid Chloride Penetration Test (RCPT), and finally, the elevated temperature test. Weight loss, strength loss, and physical observations of the acid and temperature effects of SCC mixes were evaluated. Also, the study focuses on the cost and sustainable index of SCC mixes and compares them with OPC mixes. From the experimental data analysis, it was observed that the developed SCC showed excellent physical and mechanical properties with a considerable reduction in cement content. SCC specimens with FA and EPA exhibit excellent acid and temperature resistance. Following the sustainable analysis, it was noted that SCC mixes reduce about 15–17.2% of carbon emissions compared to the OPC mix.

Structural concrete has become a highly preferable building material in the construction industry due to its versatile characteristics, such as workability, strength, and durability. When concrete structures are exposed to fire, the mechanical properties of concrete degrade significantly. The research on the residual mechanical properties of concrete after exposure is necessary, particularly for the repair and rehabilitation of concrete elements and for the stability of the infrastructure. Factors, such as the grade of concrete, the effect of temperature exposure, and rapid water cooling, affect the residual strength characteristics of concrete. Considering these factors, the present investigation evaluates the mechanical properties of concrete using different grades, such as those ranging from 20 to 50 MPa, with an increment of 10 MPa. The specimens were exposed to different durations of fire from 15 to 240 min, following the standard rate of heating. A loss of strength was observed after fire exposure for all the grades of concrete. The rate of reduction in tensile and flexural strengths of the concrete was greater than that of compressive strength. The experimental results also showed that the strength reduction is greater for M50 than M20 concrete concerning the duration of heating. A microstructure evaluation confirmed the extent of damage to concrete under varied temperature conditions.

The increase in the population creates an increased demand for construction activities with eco-friendly, sustainable, and high-performance materials. Insulated concrete form (ICF) is an emerging technology that satisfies the sustainability demands of the construction sector. ICF is a composite material (a combination of expanded polystyrene (EPS) and geopolymer concrete (GPC)) that enhances the performance of concrete (such as thermal insulation and mechanical properties). To investigate the axial strength performance, five different types of prototypes were created and tested. Type I (without reinforcement): (a) hollow EPS without concrete, (b) alternative cells of EPS filled with concrete, (c) and all the cells of EPS filled with concrete; and Type II (with reinforcement): (d) alternative cells of EPS filled with concrete; (e) and all the cells of EPS filled with concrete. Amongst all the five prototypes, two grades of GPC were employed. M15 and M20 grades are used to examine the effectiveness in terms of cost. For comparing the test results, a reference masonry unit was constructed with conventional clay bricks. The main aim of the investigation is to examine the physical and mechanical performance of sandwich-type ICFs. The presence of polystyrene in ICF changes the failure pattern from brittle to ductile. The result from the study reveals that the Type II prototype, i.e., the specimen with all the cells of EPS filled with concrete and reinforcement, possesses a maximum load-carrying capacity greater than the reference masonry unit. Therefore, the proposed ICF is recommended to replace the conventional load-bearing system and non-load-bearing walls.