The 3D micro- and nanostructure of wood has extensively been employed as a template for cost-effective and renewable electronic technologies. However, other electroactive components, in particular native lignin, have been overlooked due to the absence of an approach that allows access of the lignin through the cell wall. In this study, we introduce an approach that focuses on establishing conjugated-polymer-based electrical connections at various length scales within the wood structure, aiming to leverage the charge storage capacity of native lignin in wood-based energy storage electrodes. We demonstrate that poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) PEDOT/PSS, integrated within the cell wall lumen, can be interfaced with native lignin through the wood cell wall through in situ polymerization of a water-soluble S-EDOT monomer. This approach increases the capacitance of the conductive wood to 315 mF cm-2 at a scan rate of 5 mV s-1, which is seven and, respectively, two times higher compared to the capacitance of conductive wood made with the single components PEDOT/PSS or S-PEDOT. Moreover, we show that the capacitance is contributed by both the electroactive polymers and native lignin, with native lignin accounting for over 70% of the total charge storage capacity. We show that accessing native lignin through in situ creation of electrical interconnections within the wood structure offers a pathway toward sustainable, wood-based electrodes with improved charge-storage capacity for applications in electronics and energy storage.

In today’s digital era, electronics are integral to most activities in our daily lives, offering swift and global communication, powerful data processing tools, and advanced sensor devices. However ...

The nature of mass transport in plants has recently inspired the development of low-cost and sustainable wood-based electronics. Herein, we report a wood electrochemical transistor (WECT) where all three electrodes are fully made of conductive wood (CW). The CW is prepared using a two-step strategy of wood delignification followed by wood amalgamation with a mixed electron-ion conducting polymer, poly(3,4-ethylenedioxythiophene)–polystyrene sulfonate (PEDOT:PSS). The modified wood has an electrical conductivity of up to 69 Sm ⁻¹ induced by the formation of PEDOT:PSS microstructures inside the wood 3D scaffold. CW is then used to fabricate the WECT, which is capable of modulating an electrical current in a porous and thick transistor channel (1 mm) with an on/off ratio of 50. The device shows a good response to gate voltage modulation and exhibits dynamic switching properties similar to those of an organic electrochemical transistor. This wood-based device and the proposed working principle demonstrate the possibility to incorporate active electronic functionality into the wood, suggesting different types of bio-based electronic devices.