Rafał Bogucki

The purpose of this study was to analyze the effects of phase-change components on the properties of geopolymer foams. Geopolymer foams are lightweight foamed geopolymers that are characterized by a high degree of porosity. Phase change materials, on the other hand, are compounds that, when added to a material, allow it to absorb, store, and then release large amounts of energy. Three types of PCMs, i.e., MikroCaps, GR42, and PX25, were introduced at 15% by weight. Geopolymer materials were produced based on silica fly ash, and hydrogen peroxide H₂O₂ was used to foam the geopolymer structure. The PCM geopolymer composites were cured at 60 °C. The produced materials were tested for physical, chemical, and thermal properties. The tests included oxide and mineral composition analysis of the base material, PCM particle size analysis, apparent density and porosity tests on the foams, water leachability tests, thermal tests (λ, Cv, Cp, α), and structural and textural analysis. The most relevant tests to confirm the performance of the phase-change materials were thermal tests. With the introduction of PCMs, volumetric heat capacity increased by as much as 41% and specific heat by 45%, and thermal diffusivity decreased by 23%. The results confirm the great potential of geopolymer composites as modern insulation materials for buildings and structures.

The main motivation for this study was to improve implant materials. The influence of silver and gold on the structure and mechanical properties of Mg–Nd–Zr alloy was studied. In the work, quantitative and qualitative evaluation of the structural components of magnesium alloy with noble metal additives was performed. The research methods used were investigation of the mechanical properties and observation of micro– and macrostructures. The results showed that modification of magnesium alloy with Ag and Au contributes to the formation of spherical intermetallics of smaller size groups, which become additional centers of crystallization and grind the cast structure. The best composition from additional alloying with silver and gold was determined. Their positive effect on the strength and ductility properties of the metal was established. Preclinical and clinical testing was performed and the prospects for noble metal modification of bioabsorbable magnesium alloy for implant production usage were shown.

Additive manufacturing technologies are increasingly used in the production of semi-finished workpieces intended for further processing. This entails the need to investigate the machinability and final properties of such products. Comparative research on wire electrical discharge machining (WEDM) processes performed with two kinds of AISI 316L stainless steel workpieces is presented in this paper. The first workpiece was made by selective laser melting (SLM), while the second one was casting. Both working materials were cut with current values ranging from 8 to 72 amps. A comparison of roughness, structure and chemical composition of machined surfaces was performed between the two kinds of specimens. For the SLM sample, parameters of the cutting process that provide relatively low surface roughness (Ra ≤ 10 µm) with the simultaneous maximization of the process efficiency were determined. It was found that in the case of applying high current values (72 amp.), more favorable properties of the treated surface were obtained for the SLM sample than for the cast one.

The aspect of drug delivery is significant in many biomedical subareas including tissue engineering. Many studies are being performed to develop composites with application potential for bone tissue regeneration which at the same provide adequate conditions for osteointegration and deliver the active substance conducive to the healing process. Hydroxyapatite shows a great potential in this field due to its osteoinductive and osteoconductive properties. In the paper, hydroxyapatite synthesis via the wet precipitation method and its further use as a ceramic phase of polymer–ceramic composites based on PVP/PVA have been presented. Firstly, the sedimentation rate of hydroxyapatite in PVP solutions has been determined, which allowed us to select a 15% PVP solution (sedimentation rate was 0.0292 mm/min) as adequate for preparation of homogenous reaction mixture treated subsequently with UV radiation. Both FT-IR spectroscopy and EDS analysis allowed us to confirm the presence of both polymer and ceramic phase in composites. Materials containing hydroxyapatite showed corrugated and well-developed surface. Composites exhibited swelling properties (hydroxyapatite reduced this property by 25%) in simulated physiological fluids, which make them useful in drug delivery (swelling proceeds parallel to the drug release). The short synthesis time, possibility of preparation of composites with desired shapes and sizes and determined physicochemical properties make the composites very promising for biomedical purposes.