Xiaoming Wang

Unbound permeable aggregate base (UPAB) materials with strong load-transmitting skeleton yet adequate inter-connected pores are desired for use in the sponge-city initiative. However, the micro-scale fabric evolution and instability mechanism of macroscopic strength behavior of such UPAB materials still remain unclear. In this study, virtual monotonic triaxial compression tests were conducted by using the discrete element method (DEM) modeling approach on specimens with different gradations quantified by the parameter of gravel-to-sand ratio (G/S). The realistic aggregate particle shape and inter-particle contact behavior were properly considered in the DEM model. The micromechanical mechanisms of the shearing failure of such UPAB materials and their evolution characteristics with G/S values were disclosed from contact force chains, microstructures, and particle motion. It was found that the proportion of rotating particles in the specimens decreased and the proportion of relative sliding between particles increased as the content of fine particles decreased. The plastic yielding of the specimens originated from the failure of contact force chains and the occurrence of the relative motion between particles, while the final instability was manifested by the large-scale relative motion among particles along the failure plane (i.e., changes in the internal particle topology). By comparing the macroscopic strength, microstructure evolution, and particle motion characteristics of the specimens with different G/S values, it was found that the specimens with G/S value of 1.8 performed the best, and that the G/S value of 1.8 could be regarded as the threshold for separating floating dense and skeletal gap type packing structures. The variation of Euler angles of rotating particles was significantly reduced in the particle size range of 4.75 mm to 9.50 mm, indicating that this size range separates most of the particles from rolling and sliding. Since particle rolling and sliding behavior are directly related to shear strength, this validates the rationality of the parameter G/S for controlling and optimizing gradations from the perspective of particle movement. The findings could provide theoretical basis and technical guidance for the effective design and efficient utilization of UPAB materials.

Rail fasteners are among the key components of ballasted track of high-speed railway due to their functionality of fixing rails to sleepers. The failure of rail fastening system hinders the transmission of train loads to underlying track substructure and therefore endangers the operation safety and longevity of ballasted track. This paper first established a three-dimensional (3D) numerical model of the train-ballasted track-subgrade coupling system by integrating multibody dynamics (MBD) and finite element method (FEM). Numerical simulations were then performed to investigate the effects of different patterns of rail fastener failure (i.e., consecutive single-side, alternate single-side, and consecutive double-side) on critical dynamic responses of track structures, train running stability, and operation safety. The results show that the resulting influences of different patterns of rail fastener failure descend in the order of consecutive double-side failure, consecutive single-side failure, and alternate single-side failure. As the number of failed fasteners increases, the range where dynamic responses of track structures are influenced extends, and the failure of two consecutive single-side fasteners exerts a similar influence as that of four alternate single-side fasteners. The failure of single-side fasteners affects dynamic responses of the intact side of track structures relatively insignificantly. The influence of rail fastener failure on track structures exhibits hysteresis, thus indicating that special attention needs to be paid to locations behind failed fasteners during track inspection and maintenance. The occurrence of the failure of two or more consecutive fasteners demands timely maintenance work in order to prevent aggravated deterioration of track structures. The findings of this study could provide useful reference and guidance to smart track condition assessment and condition-based track maintenance.

The quality of compaction of unbound aggregate materials with permeable gradation plays a vital role in their field performance; however, there are currently few unanimously accepted techniques or quality control criteria available for ensuring adequate compaction of such materials in either laboratory or field applications. This paper presented testing results of a laboratory gyratory compaction study where the combinations of gyratory parameters were properly designed using the orthogonal array theory. Innovative real-time particle motion sensors were employed to record particle movement characteristics during the compaction process and provide a meso-scale explanation about compaction mechanisms. Particle abrasion and breakage were also quantified from particle shape digitized from the three-dimensional (3D) laser scanner before and after compaction. The optimal combination of gyratory parameters that yields the best compaction performance was determined from the orthogonal testing results with the relative importance of major influencing parameters ranked accordingly. Meso-scale particle movement at the upper center and center side positions of the specimen are promising indicators of compaction quality. The gyratory compaction process can be consistently divided into three distinct stages according to both macro-scale performance indicators and meso-scale particle movement characteristics. A statistically significant bi-linear relationship was found to exist between relative breakage index and maximum abrasion depth, whereas the quality of compaction and the extent of particle breakage appear to be positively correlated, thus necessitating the cost-effective balance between them. The results of this study could provide technical insights and guidance to field compaction of unbound permeable aggregates.

We report observation of electron self-injection and acceleration in a plasma accelerator driven by the Texas petawatt laser at 1017 cm-3 plasma density, an order of magnitude lower density than previous self-injected laser-plasma accelerators.