Muhammad Asif Hussain

Recently, driven by a growing focus on environmental sustainability and cost-effectiveness, researchers have shown a keen interest in creating useful materials from bio-wastes, particularly for their potential applications in the biomedical field. Current research has been conducted on the impact of date seed powder (DSP) on hydroxyapatite (HA) formation, specifically in relation to the promotion of bone health and regeneration. HA is an essential component of bone tissue and plays a crucial role in maintaining bone strength and structure. Date seed (DS) was used in two forms i.e., grains and powder, with unmodified and modified surface chemistries. Prepared composites were tested in vitro by soaking them in simulated body fluid (SBF). X-ray Diffraction (XRD) and Fourier Transform Infra-Red (FTIR) confirmed HA formation in all soaked samples. Thermogravimetric analysis (TGA) results indicated an improvement in thermal stability after soaking, suggesting a higher concentration of HA. Unsoaked samples were observed to have higher heat flow than soaked samples. The high gel content (GCs) over 90% and low hydrophilicity (less than 5%) of DSP-based composites were proven to be beneficial in HA nucleation. Antibacterial activity showed that the addition of DS filler yielded superior results compared to the pristine sample. Additionally, the modified samples demonstrated better antibacterial results than the unmodified ones.

Microbial fuel cell (MFC) technology is anticipated to be a practical alternative to the activated sludge technique for treating domestic and industrial effluents. The relevant literature mainly focuses on developing the systems and materials for maximum power output, whereas understanding the fundamental electrochemical characteristics is inadequate. This experimental study uses a double-chamber MFC having graphite electrodes and an anion-exchange membrane to investigate the electrochemical process limitations and the potential of bioelectricity generation and dairy effluent treatment. The results revealed an 81% reduction in the chemical oxygen demand (COD) in 10 days of cell operation, with an initial COD loading of 4520 mg/L. The third day recorded the highest open circuit voltage of 396 mV, and the maximum power density of 36.39 mW/m² was achieved at a current density of 0.30 A/m². The electrochemical impedance spectroscopy analysis disclosed that the activation polarization of the aerated cathode was the primary factor causing the cell’s resistance, followed by the ohmic and anodic activation overpotentials.

Nanostructured materials with optical transmittance with sufficient electrical conductivity are feasible for the transparent electrical devices and optoelectronic applications. Copper (Cu) possesses inherent superior electrical conductivity. Cu thin films on glass substrates provide the basic design understanding of the transparent electrodes for humidity sensors and solar cells applications. To understand the fundamental fabrication and electrical properties, a single-step facile fabrication approach was applied for Cu nanofilms through the DC sputtering method. Correlation of thickness of Cu nanofilms with optical and electrical properties was established. Parameters such as current, voltage, vacuum pressure, and time of coating were varied to develop different thickness of metal coating. Under optimized conditions of 10⁻¹ torr vacuum, 1.45 KV voltage, and 4–6 min coating time, a conductive path is successfully established. A 1 min coated sample demonstrated resistance of 4000 ohm and conductance of a 6 min coated sample was raised to 56 m-mho. A higher surge of voltage assisted the production of relatively thick and uniform coatings with the crystallite size of 12 nm. The average coating thickness of 19.8 nm and roughness of 4.5 nm was obtained for a 5 min coated sample through AFM analysis. Further, it was observed that uniform nanostructured coating is essential to establish a mean free path of coated particles.