By enhancing the thermal properties of cement-based building materials, energy consumption and carbon dioxide (CO₂) emissions related to space conditioning in buildings can be alleviated. This study aims to present cement-based composites reinforced by textile fibers for application in building and construction. Several lightweight coating mortars were produced by partially replacing the sand in the mix with different percentages of textile waste. Mechanical and thermal characterizations of the reinforced cementitious composites were performed. The results showed that the thermal conductivity of cementitious compounds decreased as the proportion of reinforcing material in the mixture increased. In terms of mechanical properties, the textile slightly reduced the compressive strength of cementitious mortar, while it improved the flexural strength. A numerical study was then performed to derive the actual impact of these reinforced materials on the thermal behavior of a building element using COMSOL Multiphysics. Numerous configurations of walls coated with different mortar mixtures were studied. The results showed that coating both sides of a building wall with 20 mm of textile-reinforced mortar reduced the internal temperature by 1.5 °C. Thus, the application of these thermally improved mortars as coating mortars appears to be a relevant solution to enhance the thermal performance of buildings.

Six supplementary cementitious materials (SCMs) were identified to be incorporated in concrete exposed to high-temperature cycling conditions within the thermal energy storage literature. The selected SCMs are bauxite, chamotte, ground granulated blast furnace slag, iron silicate, silica fume, and steel slag. A microstructural characterization was carried out through an optical microscope, X-ray diffraction analysis, and FT-IR. Also, a pozzolanic test was performed to study the reaction of SCMs silico-aluminous components. The formation of calcium silica hydrate was observed in all SCMs pozzolanic test. Steel slag, iron silicate, and ground granulated blast furnace slag required further milling to enhance cement reaction. Moreover, the tensile strength of three fibers (polypropylene, steel, and glass fibers) was tested after exposure to an alkalinity environment at ambient temperature during one and three months. Results show an alkaline environment entails a tensile strength decrease in polypropylene and steel fibers, leading to corrosion in the later ones.