Germana Pasquino

Pultrusion is a highly efficient continuous process to manufacture advanced fiber-reinforced composites. The injection pultrusion variant permits a higher control of the resin flow, enabling the manufacturing of a high reinforcement volume fraction. Moreover, it reduces the emission of volatile compounds that are dangerous for the operators and for the working environment. The present study proposes an experimental analysis of injection pultrusion in three different operative conditions. In particular, the activity focused on the effects of the temperature setup on the thermochemical and rheological behaviors of the resin system and on the interaction between the processed materials and the pultrusion die wall. The setup of the parameters was selected to evidence the behavior of the viscous interaction during the thermoset transition to the solid state, which is particularly challenging due to the localization of high adhesive forces related to the sharp increase in resin viscosity. Microscope observations of the cross-sections were performed to discuss the effects of the process parameters.

The present work focuses on the pultrusion of pre-impregnated glass-reinforced polypropylene tapes. An appositely designed laboratory-scale pultrusion line, consisting of a heating/forming die and a cooling die, was used. The temperature of the advancing materials and the pulling force resistance were measured by using thermocouples embedded in the pre-preg tapes and a load cell. From the analysis of the experimental outcomes, we gained insight into the nature of the material–machinery interaction and the transitions of the polypropylene matrix. The cross-section of the pultruded part was analyzed by microscope observation to evaluate the distribution of the reinforcement inside the profile and the presence of internal defects. Three-point bending and tensile testing were conducted to assess the mechanical properties of the thermoplastic composite. The pultruded product showed good quality, with an average fiber volume fraction of 23% and a limited presence of internal defects. A non-homogenous distribution of fibers in the cross-section of the profile was observed, probably due to the low number of tapes used in the present experimentation and their limited compaction. A tensile modulus and a flexural modulus of 21.5 GPa and 15.0 GPa, respectively, were measured.

Solar power is a sustainable and affordable source of energy, and has gained interest from academies, companies, and government institutions as a potential and efficient alternative for next-generation energy production. To promote the penetration of solar power in the energy market, solar-generated electricity needs to be cost-competitive with fossil fuels and other renewables. Development of new materials for solar absorbers able to collect a higher fraction of solar radiation and work at higher temperatures, together with improved design of thermal energy storage systems and components, have been addressed as strategies for increasing the efficiency of solar power plants, offering dispatchable energy and adapting the electricity production to the curve demand. Manufacturing of concentrating solar power components greatly affects their performance and durability and, thus, the global efficiency of solar power plants. The development of viable, sustainable, and efficient manufacturing procedures and processes became key aspects within the breakthrough strategies of solar power technologies. This paper provides an outlook on the application of thermal spray processes to produce selective solar absorbing coatings in solar tower receivers and high-temperature protective barriers as strategies to mitigate the corrosion of concentrating solar power and thermal energy storage components when exposed to aggressive media during service life.