Yuhua Niu

Soil contaminations by heavy metals near oilfields have been widely reported and are causing great concern. Thus, it is highly desirable to develop cost-effective materials and methods to avoid heavy metal residues contaminating soil and food. An effective, environmentally friendly, and inexpensive remediation material for heavy metal-polluted soil was designed and prepared using biochar (BC) combined with humic acid (HA) resulting from sodium humate (NaHA) simply reacting with wood vinegar (BHW). After adding BHW, the chemical fractions of copper and cadmium in the soil undergo larger changes. Meanwhile, the availability of heavy metals decreases. The maximum adsorption capacity of copper and cadmium in the soil using the BHW is larger than that only using biochar. The adsorption kinetics ensures that the adsorption process of Cd²⁺ and Cu²⁺ ions on BHW is chemical adsorption, which is best fitted using the pseudo-second-order rate equation. The thermodynamics guarantees that the metal ions adsorb on the heterogeneous surface of BHW in multilayer, which is credited to the enhancement of oxygen-containing groups in the biochar combined with the humic acid. The remediation material BHW holds promise for the immobilization of heavy metal in the soils and could be recommended based on its economic feasibility, high efficacy, and environmental safety.

Hydrochloric acid doped polyaniline (PANI) nanofibers were synthesized by an interfacial polymerization with tetrachloride as the organic solvent and with a relatively higher aniline concentration. The doped PANI nanofibers were dispersed in cyclohexanone and the dispersion was mixed with solution of polyacrylate to prepare PANI nanofibers composite coatings. It was found that the yield of the doped PANI nanofibers can be as high as 23%, though a small amount of irregular shaped PANI particles and PANI nanofibers with relatively larger diameter were also obtained. The conductivity of the PANI nanofibers based composite coatings increased with the PANI nanofibers contents and a percolation threshold of 0.2 was demonstrated. The shielding effectiveness of the PANI nanofibers based coatings increased with PANI nanofibers loadings and shielding effectiveness as high as 63 dB can be achieved with PANI nanofibers loadings of 45%. POLYM. ENG. SCI., 2008. © 2007 Society of Plastics Engineers

Polyaniline (PANI) deposited polyacrylate (PA) powders were prepared by chemical polymerization of aniline in hydrochloric acid with dispersed PA powders. The powders, after dedoped with ammonia water, were re‐doped with camphorsulfonic acid (CSA) to render them conductive, and conductive PANI/polyacrylate composite coatings (PANI/PA) were prepared by bead milling of these CSA‐doped PANI (PANI–CSA) deposited polyacrylate powders (PANI–CSA/PA). It was found that aniline was polymerized preferentially at the surfaces of the powders and PANI deposited powders were obtained as indicated by the scanning electronic microscopy images. The amount of deposited PANI increased with the aniline/polyacrylate weight ratio in feed, and no isolated PANI particles was found. UV–Vis and Fourier transformed infrared spectra indicated that the PANI layer was physically adhered to the PA powders, and not chemically. Conductivities of the PANI–CSA/PA powders and the PANI/PA coatings increased with the amounts of PANI–CSA and a percolation threshold of 0.2 and 0.3 was demonstrated, respectively. Electromagnetic interference shielding measurements showed that the shielding effectiveness of the PANI/PA coatings increased with PANI–CSA loadings, and shielding effectiveness as high as 60 dB can be achieved with the coatings. POLYM. COMPOS., 27:627–632, 2006. © 2006 Society of Plastics Engineers