Beata Swinarew

The use of modern materials in sports, in terms of chemical composition and surface texture, entails both progress in results and an increasing discrepancy in the technical parameters of the equipment used. This paper aims to demonstrate the differences between balls admitted to a league and world championships in composition, surface texture, and the influence of these parameters on the water polo game. This research compared two new balls produced by top companies producing sports accessories (Kap 7 and Mikasa). To obtain the goal, the measurement of the contact angle, analysis of the material using Fourier-transform infrared spectroscopy, and optical microscopic evaluation were used. The analysis of the surface free energy shows significant differences (Kap 7 32.16 mJ/m², Mikasa 36.48 mJ/m²). In the case of both balls, anisotropies of the structure of the furrows were observed, however, the Mikasa ball is slightly more homogeneous than the Kap 7 ball. The obtained results from the analysis of the contact angle, as well as the composition and real feedback from the players, indicated the need to standardize the material aspect of the regulations so that the sports results are repeatable every time.

This research aimed to examine the mechanical properties of polycarbonate-based composites filled with both organic and inorganic reinforcements before and after simulated environmental degradation. Series of polycarbonate-based samples were prepared in the form of thin tapes. Their rheological properties were examined. Then, the samples were exposed to artificial environmental conditions. Finally, their rheological properties were examined once more, and the results were compared with those obtained for untreated samples. This paper presents basic research on the application of inorganic fillers to polycarbonate in order to determine the influence of the filler on the behavior of the obtained material. The aim of the work was to determine the usefulness and purpose of using this type of filler in polycarbonates for applications in contact with ultraviolet radiation, especially medical applications.

In the era of modern medicine, the number of invasive treatments increases. Artificial devices used in medicine are associated with an increased risk of secondary infections. Bacterial biofilm development observed on the implanted surface is challenging to treat, primarily due to low antibiotics penetration. In our study, the preparation of a new polycarbonate composite, filled with nanosilver, nanosilica and rhodamine B derivative, suitable for three-dimensional printing, is described. Polymer materials with antimicrobial properties are known. However, in most cases, protection is limited to the outer layers only. The newly developed materials are protected in their entire volume. Moreover, the antibacterial properties are retained after multiple high-temperature processing were performed, allowing them to be used in 3D printing. Bacterial population reduction was observed, which gives an assumption for those materials to be clinically tested in the production of various medical devices and for the reduction of morbidity and mortality caused by multidrug-resistant bacteria.

Mono- and dipotassium salts of dipropylene glycol were applied for the polymerization of propylene oxide in mild conditions, i.e., tetrahydrofuran solution at ambient temperature. The structure of polymers was investigated by use of ¹³C NMR and MALDI-TOF techniques. The structure depends strongly on the kind of initiator and additives that are used such as coronand 18-crown-6 and dipropylene glycol. The lowest unsaturation, represented by allyloxy starting groups, has the polymer obtained by use of monopotassium salt without the ligand. The highest unsaturation degree is for the polymer synthesized in the presence of dipotassium salt–activated 18-crown-6. This polymer, obtained at high initial monomer concentration and low initial concentration of initiator, consists of two fractions, i.e., a low molar mass fraction (M_n = 9400) containing mainly macromolecules with alkoxide starting and end groups and a much higher molar mass fraction (M_n = 29500 g/mol) containing macromolecules with allyloxy starting groups and alkoxide or hydroxyl end groups. Addition of free glycol to this system decreases the molar mass of polymers. Similar results were obtained by use of dipotassium salts of other glycols. The mechanisms of the studied processes are discussed.