The study and subsequent analysis of the interaction of calcium sulfate with added citric acid and with two additional proportions of carbon fibers of different lengths has been based on the IMR and D Method for its realization. The purpose of this work is the study of the physical and mechanical behavior of the resulting material between the intimate mixture of calcium sulfate with additives and carbon fibers, justifying said work with a link to the Sustainable Development Goals (SDG) regarding the benefits that the Calcium sulfate has contributed to civil society since times dating back to ancient Egypt. We find ourselves with a material of which the energy used in its manufacture is far from that required by steel or cement, and construction with this new compound is in a much higher stage than construction with adobe. Therefore, this is a compound that can be developed for a wide variety of applications. The novelty of this study is the inclusion of polymeric fibers in a material used over the centuries to improve its mechanical properties. With these improvements we will be able to reduce thicknesses in manufacturing, which implies a reduction in manufacturing energy and weight structures in buildings, which should be studied and analyzed in the future. The kneading of calcium sulfate with long fibers at high percentages complicates not only the results, but also the manufacturing process. As representative results of the study, we can indicate that a composite material with high mechanical capacity has been achieved, with maximum values of flexural strength of 8.12 N/mm² and compression strength of 17.58 N/mm².

In this paper, we evaluate different gypsum coating additives that are available on the market, which are categorized by their chemical bases. The results will serve as a reference for future investigations of new additive bases in order to improve the properties of gypsum. As such, the objective of the this study is to assess the workability, mechanical behavior, and crystalline structure of calcium sulfate combined with different retarding and fluidifying bases, including melamine bases, which have a compressive strength of 19.32 N/mm² and handling times with polycarbonate salts of up to 117.58 min. The following study presents the results of standard mechanical tests, analyzing semi-hydrated calcium sulfate (without additives) as a reference, along with the addition of melamines, synthetic melanin polymers, polycarbonate salts, polycarboxylates, and a polycarboxylic acid (citric acid). We already know that the addition of these additives will modify the mechanical properties of calcium sulfate, such as the Shore C surface hardness, flexural strength, modulus of elasticity, and compression resistance, which is the object of this study.