Walid Abotbina

The rapid use of petroleum resources coupled with increased awareness of global environmental problems associated with the use of petroleum-based plastics is a major driving force in the acceptance of natural fibers and biopolymers as green materials. Because of their environmentally friendly and sustainable nature, natural fibers and biopolymers have gained significant attention from scientists and industries. Cassava (Manihot esculenta) is a plant that has various purposes for use. It is the primary source of food in many countries and is also used in the production of biocomposites, biopolymers, and biofibers. Starch from cassava can be plasticized, reinforced with fibers, or blended with other polymers to strengthen their properties. Besides that, it is currently used as a raw material for bioethanol and renewable energy production. This comprehensive review paper explains the latest developments in bioethanol compounds from cassava and gives a detailed report on macro and nano-sized cassava fibers and starch, and their fabrication as blend polymers, biocomposites, and hybrid composites. The review also highlights the potential utilization of cassava fibers and biopolymers for industrial applications such as food, bioenergy, packaging, automotive, and others.

Great advances have been made in the preparation of bioplastics and crude oil replacements to create a better and more sustainable and eco-friendly future for all. Here, we used cassava bagasse fibers at different ratios as reinforcement material to enhance the properties of black seed w-cornstarch films using the facile solution casting technique. The reinforced films showed compact and relatively smoother structures without porosity. The crystallinity values increased from 34.6 ± 1.6% of the control to 38.8 ± 2.1% in sample CS-BS/CB 9%, which reflects the mechanical properties of the composite. A gradual increase in tensile strength and elastic modulus was observed, with an increase in loading amounts of 14.07 to 18.22 MPa and 83.65 to 118.32 MPa for the tensile strength and elastic modulus, respectively. The composite film also exhibited faster biodegradation in the soil burial test, in addition to lower water absorption capacity. Using bio-based reinforcement material could significantly enhance the properties of bio-based packaging materials. The prepared hybrid composite could have a promising potential in food packaging applications as a safe alternative for conventional packaging.

This work aims to develop cornstarch (CS) based films using fructose (F), glycerol (G), and their combination (FG) as plasticizers with different ratios for food packaging applications. The findings showed that F-plasticized film had the lowest moisture content, highest crystallinity among all films, and exhibited the highest tensile strength and thermostability. In contrast, G-plasticized films showed the lowest density and water absorption with less crystallinity compared to the control and the other plasticized film. In addition, SEM results indicated that FG-plasticized films had a relatively smoother and more coherent surface among the tested films. The findings have also shown that varying the concentration of the plasticizers significantly affected the different properties of the plasticized films. Therefore, the selection of a suitable plasticizer at an appropriate concentration may significantly optimize film properties to promote the utilization of CS films for food packaging applications.