Dan Buhățel

Background and Objectives: The aim of this in vitro study was to evaluate the effect of simulated gastric acid associated with toothbrushing on the surface condition of three resin-modified glass-ionomer cements (RMGIC). Materials and Methods: One hundred and sixty samples of each material were obtained and included in three study groups according to the tested material: Group I (Ionolux, VOCO GmbH, Cuxhaven, Germany); Group II (Vitremer, 3 M-ESPE, St. Paul, MN, USA); and Group III (Fuji II LC, GC Corporation, Tokyo, Japan). The samples were submersed in hydrochloric acid 0.01 M (pH 3.8) for 3 h and exposed to a toothbrushing procedure at a frequency of 10,000 cycles with medium and hard bristles immediately or 30 min after the acid attack. Profilometric measurements were performed by using a non-contact profilometer (Dektak XT, Bruker, Billerica, MA, USA) in order to assess the surface roughness. ANOVA and Bonferroni post hoc tests were used for the statistical analysis at a significance level of p < 0.05. Results: Exposure of RMGICs to the erosive effect of hydrochloric acid in association with toothbrushing 30 min after the chemical attack increased the surface roughness of all three RMGICs. Exposure of the three tested materials exclusively to the action of hydrochloric acid did not affect the surface roughness. Conclusions: One year of hydrochloric acid challenge associated with one year of toothbrushing with medium-hardness bristles performed 30 min after the acid attack increase the surface roughness of two of the three types of RMGIC tested (Ionolux and Fuji II LC).

This in vitro study aimed to assess the erosive effect of hydrochloric acid in association with toothbrushing procedure on the surface condition of three bulk-fill composite resins used for direct restoration. A total of 480 samples (160 from each composite resin): X-tra Fil (VOCO, Germany)—group A, Filtek Bulk-fill Posterior (3M-ESPE, St. Paul, MN, USA)—group B, G-aenial Posterior (GC Japan)—group C were prepared, submitted to chemical attack for 60 min with hydrochloric acid 30% and, subsequently, submitted to the abrasive effect of toothbrushing using 10,000 cycles with medium and hard bristles, at three different times (immediately and after 30 min after acid attack or without any chemical attack). The surface roughness of the samples was measured using a noncontact profilometer (Dektak XT, Bruker, Billerica, MA, USA). The values were analyzed using ANOVA and post hoc Bonferroni tests, with a p < 0.05. Chemical attack for 60 min associated with one year of toothbrushing with toothbrushes having medium or hard bristles increase the surface roughness of tested bulk-fill composite resins. No differences were recorded between toothbrushing with medium or firm bristles immediately or 30 min after acidic challenge for each of the three bulk-fill composite resins. Exposure to hydrochloric acid determines no effect on surface roughness of bulk-fill composite resins.

In Romania, the term dental malpractice is relatively new compared to medical malpractice. The common premises that underlie these iatrogenics have made doctors more vigilant about treatment and achieving the desired results. At the same time, the conditions of medical liability are consistent with those of civil liability, namely: damage, wrongdoing, guilt, and causation. To counteract these effects, public attention has been focused in recent years on patients' rights (involving, causes, effects, informed consent of the patient regarding the collection of personal data, informing the patient about the work itself, and possible complications which may occur postoperatively). As a result, the number of reported cases of malpractice has increased markedly in recent years.