Qingbo Wang

CdZnTe (CZT) is a new type of compound semiconductor that has emerged in recent years. Compared to other semiconductor materials, it possesses an ideal bandgap, high density, and high electron mobility, rendering it an excellent room-temperature composite semiconductor material for X-ray and γ-ray detectors. Due to the exceptional performance of CZT material, detectors manufactured using it exhibit high energy resolution, spatial resolution, and detection efficiency. They also have the advantage of operating at room temperature. CZT array detectors, furthermore, demonstrate outstanding spatial detection and three-dimensional imaging capabilities. Researchers worldwide have conducted extensive studies on this subject. This paper, building upon this foundation, provides a comprehensive analysis of CZT crystals and CZT array detectors and summarizes existing research to offer valuable insights for envisioning new detector methodologies.

CdZnTe (CZT) is a new type of compound semiconductor that has emerged in recent years. Compared to other semiconductor materials, it possesses an ideal bandgap, high density, and high electron mobility, rendering it an excellent room-temperature composite semiconductor material for X-ray and γ-ray detectors. Due to the exceptional performance of CZT material, detectors manufactured using it exhibit high energy resolution, spatial resolution, and detection efficiency. They also have the advantage of operating at room temperature. CZT array detectors, furthermore, demonstrate outstanding spatial detection and three-dimensional imaging capabilities. Researchers worldwide have conducted extensive studies on this subject. This paper, building upon this foundation, provides a comprehensive analysis of CZT crystals and CZT array detectors, summarizes existing research to offer valuable insights for envisioning new detector methodologies.

The economics and safety of reactors can be affected by the diffusion of fission products into graphite. Xenon (Xe) fission products diffusing into graphite is the most critical neutron absorber and poison that can slow down or stop the chain reaction. The transport parameters for inhibiting the xenon diffusion in graphite are therefore an important scientific problem. Self-sintered nanopore-isotropic (~40 nm) graphite (SSNG) derived from green pitch coke can decrease Xe diffusion into graphite. In this study, the surface morphology and microstructural evolution in graphite before and after irradiation, as well as after annealing, were studied with different characterization methods. A method for the measurement of diffusion coefficients of fission products’ diffusion in graphite using Rutherford backscattering spectrometry (RBS) was also reported. The SSNG substrates were implanted with Xe at a dose of 4.8 × 10¹⁵ ions/cm² and energy of 7 MeV. The RT-implanted samples were annealed in a vacuum at 650 °C for 9 h. The implanted and annealed samples were characterized using RBS. The diffusion coefficient D (Xe, 650 °C) was 6.49 × 10⁻²⁰ m²/s. The results indicate SSNG’s excellent ability to inhibit Xe diffusion and are significant for designing and evaluating the safety of nuclear reactors.

The economics and safety of reactors can be affected by the diffusion of fission products into graphite. Xenon (Xe) fission products diffusing into the graphite is the most critical neutron absorber and poison that can slow down or stop the chain reaction. The transport parameters for inhibiting the xenon diffusion in graphite are therefore the utmost scientific problem. Self-sintered nanopore-isotropic (~ 40nm) graphite (SSNG) derived from green pitch coke can decrease Xe diffusion into the graphite. In this study, a method for measurement of diffusion coefficients of fission products diffusion in graphite by Rutherford backscattering spectrometry (RBS) was reported. The SSNG substrates were implanted with Xe at a dose of 4.8×1015 ions/cm2 and energy of 7 MeV. The RT-implanted samples were annealed in a vacuum at 650°C for 9 h. The implanted and annealed samples were characterized by RBS. The diffusion coefficient D(Xe,650°C) is 6.49×10-20 m2/s. The results indicate the excellent ability to inhibit Xe diffusion of the SSNG and present significance in designing and evaluating the safety of nuclear reactors.

The diffusion behavior of iodine in micro/nano-porous graphite under high-temperature conditions was studied using analysis methods such as Rutherford backscattering Spectrometry, scanning electron microscopy, X-ray diffraction, and Raman spectroscopy. The results indicate that iodine diffusion leads to the Lattice Contractions in Microcrystals, a decrease in interlayer spacing, and a rise of defect density. And the reversal or repair of microstructure change was observed: the microcrystal size of the graphite increases, the interlayer spacing appears to return to the initial state, and the defect density decreases, upon diffusion of iodine out of iodine-loaded graphite. The comparative study comparing the iodine diffusion performance of nanoporous graphite (G400 and G450) between microporous graphite (G500), showed that nanoporous graphite exhibits a better barrier to the iodine diffusion. The study on the diffusion behavior of iodine in micro/nano-porous graphite holds substantial academic and engineering value for the screening, design, and performance optimization of nuclear graphite.

Using analysis methods such as Rutherford backscattering Spectrometry, scanning electron microscopy, X-ray diffraction, and Raman spectroscopy, the diffusion behavior of iodine in micro/nano-porous graphite under high-temperature conditions was studied. The results indicate that iodine diffusion leads to the contraction of graphite microcrystals, a decrease in interlayer spacing, and an increase in defect density, resulting in a reduction in microcrystal size. Upon diffusion of iodine out of iodine-loaded graphite, the microcrystal size of the graphite increases, the interlayer spacing appears to return to the initial state, and the defect density decreases. By comparing the iodine diffusion performance of nanoporous graphite G400 and G450 with microporous graphite G500, it was determined that nanoporous graphite exhibits better inhibition of iodine diffusion compared to microporous graphite. Studying the diffusion behavior of iodine in micro/nano-porous graphite has significant academic significance and engineering value for the screening, design, and performance optimization of nuclear graphite.

The general circuit topology and principles of low-noise high-voltage power supply are investigated to meet the requirements of the high-voltage bias application in air kerma meters. Two topologies, flyback converter and Royer converter are simulated using SPICE simulation program. The simulation results indicate that the circuit structure of the Royer converter is more complex, but it obtains lower output high voltage noise. While we develop an adjustable high-voltage power supply according to the circuit structure of the Royer converter, and tested it to ensure the design requirements for continuously adjustable output high-voltage linearity. The test results show that the linear adjustment rate is not more than ±0.0025%, the load regulation rate is less than ±0.1%, and the output ripple noise voltage percentage is less than 0.01%. These tested performance make it more suitable for accurate nuclear measurements.

Two forms of fine-grained isotropic graphite, derived from mixed fillers by the isostatic pressing method, NG (filler with 100% natural graphite flake) and 75N25C-G (mixed filler with 75 wt.% natural graphite flake and 25 wt.% calcined coke) were prepared and irradiated with 7 MeV Xe²⁶⁺ to investigate its irradiation behaviors. Grazing incidence X-ray diffraction and Raman spectra show that the initial graphitization degree of 75N25C-G is lower than that of NG, but the crystallite sizes are larger due to calcined coke in the filler particles. After irradiation, the stacking height of crystallite sizes along c-axis directions (L_c) of NG increased, and Lc of 75N25C-G decreased. This can be attributed to irradiation-induced catalytic graphitization of calcined coke, and is also the reason that the dislocation density of 75N25C-G increases slower than that of NG. After irradiation, the crystallite sizes along a-axis directions (L_a) of NG and 75N25C-G reduced, but this trend was more obvious in irradiated 75N25C-G; this was closely related to the change of the surface morphology. The results show that the effect of the content of natural graphite flakes in the filler on the initial graphitization degree determines the difference in microstructure evolution caused by irradiation.

The detection of α particles is of great significance in military and civil nuclear facility management. At present, the contact method is mainly used to detect α particles, but its shortcomings limit the broad application of this method. In recent years, preliminary research on noncontact α-particle detection methods has been carried out. In this paper, the theory of noncontact α-particles detection methods is introduced and studied. We also review the direct detection and imaging methods of α particles based on the different wavelengths of fluorescence photons, and analyze the application and development of this method, providing an important reference for researchers to carry out related work.