Miao Yu

This study investigated the noise reduction performance of porous asphalt concrete (PAC) pavement under tire–pavement coupling conditions, addressing the limitations of field measurements and laboratory testing. First, tire excitation amplitude parameters were determined based on vibrational contact operational scenarios. Then, finite element simulations were conducted to systematically analyzing the tire–pavement coupling noise characteristics of PAC pavement. The results indicate that PAC pavement effectively reduces the air pumping noise due to its highly porous internal structure, leading to significant noise attenuation. Furthermore, the study examined the key factors influencing the tire–pavement coupling noise in PAC pavement. When maintaining constant vehicle parameters (300 kg load, 60 km/h speed), pavement thickness became the critical noise-control variable, achieving minimum vibration at 6 cm surface layer thickness. Additionally, tire tread depth (5–17 mm) and mold release angle (0–30°) had a more pronounced impact on the air pumping noise compared to groove width (20–60 mm). Increasing the mold release angle and reducing tread depth effectively mitigated the air pumping noise. However, the tire–pavement coupling noise in PAC pavement increased considerably with increasing vehicle speed and load. Particularly, as the speed increased from 30 km/h to 60 km/h, the growth of the air pumping noise was most pronounced, revealing an acoustic transition of tire–pavement coupling noise from vibration-dominated to air-pumping-dominated mechanisms.

Preventive maintenance treatments are widely applied to asphalt pavements to mitigate deterioration and extend service life. This study evaluated four common technologies: a high-elasticity ultra-thin overlay, an Stone Mastic Asphalt (SMA)-10 thin overlay, micro-surfacing (MS-III), and a chip seal. Laboratory testing focused on skid resistance, surface texture, and low-temperature cracking resistance. Skid resistance was measured with a tire–pavement dynamic friction analyzer under controlled load and speed, while surface macrotexture was assessed using a laser scanner. Low-temperature cracking resistance was determined through three-point bending beam tests at −10 °C. The results showed that chip seal achieved the highest initial friction and texture depth, immediately enhancing skid resistance but exhibiting rapid texture loss and gradual friction decay. Micro-surfacing also demonstrated good initial skid resistance but experienced a sharp reduction of over 30% due to fine aggregate polishing. By contrast, the high-elastic ultra-thin overlay and SMA thin overlay provided more stable skid resistance, lower long-term friction loss, and excellent crack resistance. The polymer-modified ultra-thin overlay achieved the highest low-temperature bending strain ≈40% higher than untreated pavement, indicating superior crack resistance, followed by the SMA thin overlay. Micro-surfacing with a chip seal layer only slightly improved low-temperature performance. Overall, the high-elastic ultra-thin overlay proved to be the most balanced preventive maintenance option under heavy-load traffic and cold climate conditions, combining durable skid resistance with enhanced crack resistance.

In this study, a wear-resistant ultra-thin wear layer was fabricated with polyurethane as an adhesive to investigate its durability for pavement applications. Its road performance was investigated based on indoor tests. First, the abrasion test was performed using a tire–pavement dynamic friction analyzer (TDFA), and the surface elevation information of the wear layer was obtained by laser profile scanning. The relationship between the anti-skid properties of the wear layer and the macro-texture was analyzed. Second, a Fourier infrared spectrometer and scanning electron microscope were employed to analyze the evolution of polyurethane aging properties in the pull-out test and accelerated ultraviolet (UV) aging test. The results showed that the mean profile depth (MPD), arithmetic mean wavelength of contour (λa), surface wear index (SBI), stage mass loss rate (σ), and total stage mass loss rate (ω) of the abrasive layer aggregate had significant multivariate quadratic polynomial relationships with the skidding performance of the abrasive layer. The tensile strength of the polyurethane ultra-thin abrasive layer decreased by only 2.59% after 16 days of UV aging, indicating a minimal effect of UV action on the aggregate and structural spalling of the polyurethane abrasive layer.

In order to build an appropriate prediction model of pavement friction coefficient attenuation, the effects of aggregate texture, on a basis of texture scanning and pavement testing of the dynamic friction coefficient, traffic volume, and rock characteristics on pavement slide decay resistance were studied, and the accuracy of the developed prediction model of friction coefficient was thereafter compared and analysed. First, based on the tire-pavement dynamic friction analyzer independently developed by the research group, accelerated loading tests under different traffic conditions were conducted by the orthogonal test method, and the dynamic friction coefficient of pavement during the abrasion process was recorded. At the same time, the non-contact laser profile measurement system was used to collect three-dimensional micro-texture data of coarse aggregate surface at different abrasion stages, and characteristic parameters such as height, wavelength, and shape were calculated. Second, the factors such as traffic volume and rock characteristics were incorporated, and the algorithms such as multiple linear stepwise regression, feedforward neural network, and random forest regression were adopted to develop estimation models of pavement friction. The results showed that the model constructed based on only texture feature parameters poorly represented pavement skid resistance. After introducing the two indicators of total traffic volume and rock type, the correlation coefficients of the model significantly improved, reaching 0.63, 0.58, and 0.82 respectively, indicating that the latter two factors have significant effects on the anti-skid attenuation of pavement. Moreover, the above three models can achieve satisfactory prediction results. In addition, when a large sample size can be obtained, a random forest algorithm is recommended to acquire higher prediction accuracy of pavement friction coefficient attenuation.

This study presented a finite element model of radial tire–asphalt pavement interaction using ABAQUS 6.14 software to investigate the skid resistance properties of asphalt pavement under partial tire aquaplane conditions. Firstly, the pavement profile datum acquired by laser scanning were imported to Finite Element Analysis (FEA) software to conduct the pavement modeling. Secondly, a steady state rolling analysis of a tire on three types of asphalt pavements under drying conditions was carried out. Variation laws of the friction coefficient of the radial tire on different pavements with different pavement textures, tire pressures, and loads on the tire were examined. Subsequently, calculation results of the steady state rolling analysis were transmitted to dynamic explicit analysis, and an aquaplane model of a radial tire on asphalt pavements was built by inputting the flow Euler grids. The tire–pavement adhesive characteristics under partial aquaplane conditions are discussed regarding the aquaplane model. Influences of the thickness of water film, the texture of asphalt pavement, and the rolling speed of the tire on the vertical pavement-tire contact force are analyzed. It is found that the vertical contact force between open graded friction course (OGFC) pavement and tire is the highest, followed by stone mastic asphalt (SMA) pavement and dense graded asphalt concrete (AC) pavement surface. The vertical contact force between tire and pavement will be greatly reduced, even with increasing speed or water film thickness. As tire speed increases from 70 km/h to 130 km/h, the tire–pavement contact force is reduced by about 25%. Moreover, when the thickness of water film increases from 0 (dry condition) to 4 mm and then to 12 mm, the vertical contact force reduced 50% and 15%, respectively, compared with under the dry contact condition. This study provided a key theoretical reference for safe driving on wet pavements.

The use of fiber in asphalt mixtures can improve the mixture’s tensile strength and increase its cracking resistance, but the clumping of fiber in the mixture can weaken the improvement effect. The aim of this research is to assess the properties of Sasobit treated aramid fiber modified asphalt mixture and to validate the field case study. The rutting and stripping resistance of the fiber-modified mixture was identified with the Hamburg wheel tracking device. The low-temperature cracking characteristics of the asphalt mixture were quantified with the disk-shaped compact tension test. Moreover, the dynamic modulus test was adopted to reflect the response of the mixture to different loads and frequencies. The creep slope and stripping slope decreased by 67%, and the number of passes to stripping point and fail point increased by more than 250% after fiber modification. The fracture energy, peak load, and maximum crack mouth opening displacement (CMOD) of the mixture increased more than 10% after fiber modification. The dynamic modulus, rutting parameter, and fatigue parameter of the mixture were improved after fiber modification. The fiber in the mixture improved the stiffness of the mixture at high temperatures. The tensile strength improvement at low temperatures promoted the cracking resistance of the mixture. The cracking number in the fiber modified asphalt pavement was less than that in the control asphalt pavement. Thus, fiber modification could significantly restrict the propagation of cracking in the asphalt mixture. The implementation of fiber in the project can provide experience for future fiber application in asphalt pavement.

The skid-resisting performance of pavement is a critical factor in traffic safety. Recent studies primarily analyze this behavior by examining the macro or micro texture of the pavement. It is inevitable that skid-resistance declines with time because the texture of pavement deteriorates throughout its service life. The primary objective of this paper is to evaluate the use of different asphalt pavements, varying in resilience, to optimize braking performance on pavement. Based on the systematic dynamics of tire-pavement contact, and analysis of the tire-road coupled friction mechanism and the effect of enlarging the tire-pavement contact area, road skid resistance was investigated by altering the elastic modulus of asphalt pavement. First, this research constructed the kinetic contact model to simulate tire-pavement friction. Next, the following aspects of contact behaviors were studied when braking: tread deformation in the tangential pavement interface, actual tire-pavement contact in the course, and the frictional braking force transmitted from the pavement to the tires. It was observed that with improvements in pavement elasticity, the actual tire-pavement contact area increased, which gives us the ability to effectively strengthen the frictional adhesion of the tire to the pavement. It should not be overlooked that the improvement in skid resistance was caused by an increase in pavement elasticity. This research approach provides a theoretical basis and design reference for the anti-skid research of asphalt pavements.