This study investigates the potential for affordable and lightweight polymer electrolyte membrane fuel cells (PEMFCs) using lightweight flow-field plates, also referred to as bipolar plates. A comparative analysis was conducted on the performance of metal-coated and uncoated three-dimensional (3D)-printed flow-field plates, as well as that of a conventional graphite flow-field plate. The fabrication of these lightweight flow-field plates involved the application of sputtering and 3D printing technologies. The polarization curves and corresponding electrochemical impedance spectra of PEMFCs with metal-coated 3D-printed, uncoated 3D-printed, and graphite flow-field plates were measured. The results demonstrate that the metal-coated 3D-printed flow-field plate exhibits a gravimetric power density of 5.21 mW/g, while the graphite flow-field plate registers a value of 2.78 mW/g, representing an 87.4% improvement in gravimetric power density for the metal-coated 3D-printed flow-field plate compared to the graphite flow-field plate. These findings suggest the feasibility of reducing the weight of PEMFCs using metal-coated 3D-printed flow-field plates.

Polymer electrolyte membrane fuel cells were analyzed to investigate changes in the structure of the flow field and operating conditions. The cell performance, which was controlled by adjusting the width of the cathodic channel, improved as the backpressure increases. With the anodic and cathodic flow channels mismatched, the maximum power densities at 3.0 bar for a narrow cathodic channel were 1115 and 1024 mW/cm², and those for a wide cathodic channel were 959 and 868 mW/cm², respectively. The diffusion characteristics were investigated using the non-dimensional numbers Re (Reynolds), Sc (Schmidt), and Sh (Sherwood) to confirm the improvement of mass transport. The narrower the channel or the higher the operating pressure, the larger Re was and the smaller Sc and Sh became. In particular, the wider the anodic channel, the larger the value of Sh.