Sylvia De Meester

Copper joints are indispensable in electronics and the electrical power industry due to their predominant usage in battery pack manufacturing for electric vehicle). Traditional joining methods are often limited by oxidation-related challenges. Recent efforts have focused on addressing these limitations by employing solid-state techniques like ultrasonic welding (USW) for joining similar metals. USW presents attractive advantages such as a lower processing temperature and shorter weld time. This study investigates the ultrasonic welding of Cu-Cu joints with a thickness of 0.5 mm, focusing on both mechanical and metallurgical properties. The influence of key process parameters, such as the welding time, pressure and vibration amplitude, was examined in relation to the welding energy and lap shear strength. Additionally, the relationship between the input energy and lap shear strength was explored. A Pareto chart analysis revealed the standardized effects of these parameters on the welding energy and average lap shear strength. The welding time had a significant influence on the welding energy, while the vibration amplitude had the greatest impact on the joint strength. Longer weld times of 2.50 to 4 s yielded a higher lap shear strength, averaging up to 2.30 kN. Notably, a higher lap shear strength was achieved at lower welding energy levels.

Ultrasonic welding (USW) is a solid-state welding process based on the application of high frequency vibration energy to the workpiece to produce the internal friction between the faying surface and the local heat generation required to promote the joining. The short welding time and the low heat input, the absence of fumes, sparks or flames, and the automation capacity make it particularly interesting for several fields, such as electrical/electronic, automotive, aerospace, appliance, and medical products industries. The main problems that those industries have to face are related to the poor weld quality due the improper selection of weld parameters. In the present work, 0.3 mm thick copper sheets were joined by USW varying the welding time, pressure, and vibration amplitude. The influence of the process variables on the characteristics of the joints and weld strength is investigated by using the analysis of variance. The results of the present work indicate that welding time is the main factor affecting the energy absorbed during the welding, followed by the pressure and amplitude. The shear strength, on the other hand, resulted mostly influenced by the amplitude, while the other parameters have a limited effect. Regardless the welding configuration adopted, most welds registered a failure load higher than the base material pointing out the feasibility of the USW process to join copper sheets.

The demand for joining dissimilar metals has exponentially increased due to the global concerns about climate change, especially for electric vehicles in the automotive industry. Ultrasonic welding (USW) surges as a very promising technique to join dissimilar metals, providing strength and electric conductivity, in addition to avoid metallurgical defects, such as the formation of intermetallic compounds, brittle phases and porosities. However, USW is a very sensitive process, which depends on many parameters. This work evaluates the impact of the process parameters on the quality of ultrasonic spot welds between copper and aluminium plates. The weld quality is assessed based on the tensile strength of the joints and metallographic examination of the weld cross-sections. Furthermore, the welding energy is examined for the different welding conditions. This is done to evaluate the influence of each parameter on the heat input resulting from friction at the weld interface and on the weld quality. From the obtained results, it was possible to optimise parameters to achieve satisfactory weld quality in 1.0 mm thick Al–Cu plate joints in terms of mechanical and metallurgical properties.