Mohammad Soleimani

The development of advanced catalysts with innovative nanoarchitectures is critical for addressing energy and environmental challenges such as the electrochemical CO2 reduction reaction (CO2RR). In this work, we present the synthesis of an innovative copper-sulfur planar structure, Cu-S-BDC, within a metal-organic framework (MOF) catalyst, which demonstrates 100% selectivity towards formate as the sole carbon product. Structural analysis and surface characterizations reveal that Cu-S-BDC exhibits quasi-two-dimensional inorganic building units, with Cu bonded to two S-CH3 groups and one BDC linker, while carboxylate groups adopt a bridging coordination mode. This unique arrangement not only imparts remarkable structural stability but also enhances the electronic properties of the MOF, as evidenced by a narrow band gap of 1.203 eV that facilitates efficient charge transfer and increased electrochemical current density in CO2RR. Notably, it offers a Faradaic efficiency (FE) of 92% for formate at an overpotential as low as -0.4 V vs. the reversible hydrogen electrode (RHE) in an aqueous electrolyte of 1 M KOH, as well as a current density of -25.8 mA/cm2 at -0.9 V vs. RHE, averaged over 24 hours of electrolysis. This study highlights a fresh perspective in the field of MOF electrocatalysts by demonstrating that engineering the metal coordination environment can significantly enhance the electronic properties and consequently improve the electrocatalytic performance of these materials.

Investigating and understanding the intrinsic material properties of biogenic materials, which have evolved over millions of years into admirable structures with difficult to mimic hierarchical levels, holds the potential of replacing trial-and-error-based materials optimization in our efforts to make synthetic materials of similarly advanced complexity and properties. An excellent example is biogenic silica which is found in the exoskeleton of unicellular photosynthetic algae termed diatoms. Because of the complex micro- and nanostructures found in their exoskeleton, determining the intrinsic mechanical properties of biosilica in diatoms has only partly been accomplished. Here, a general method is presented in which a combination of in situ deformation tests inside an SEM with a realistic 3D model of the frustule of diatom Craspedostauros sp. (C. sp.) obtained by electron tomography, alongside finite element method (FEM) simulations, enables quantification of the Young’s modulus (E = 2.3 ± 0.1 GPa) of this biogenic hierarchical silica. The workflow presented can be readily extended to other diatom species, biominerals, or even synthetic hierarchical materials.

Determination of mechanical properties of (silica) thin films is important for the development of new applications. However, a versatile approach for small‐scale sample fabrication and in situ mechanical testing of these materials is currently lacking which can overcome the existing difficulties in conventional testing approaches. Here, it is shown that by combining focused ion beam scanning electron microscopy (FIB‐SEM) with micromanipulators free‐standing silica beams of the desired dimensions can be fabricated. Using in situ bending tests on such beams inside the SEM and finite element method simulations, the Young's modulus of thin‐film silica and the effects of gallium ion beam radiation on Young's modulus are determined. Furthermore, the effects of controlled relative humidity on the mechanical behavior of silica beams are investigated. The demonstrated FIB‐SEM approach can be extended to other materials and preparation conditions to measure, model, and optimize mechanical properties of thin films for a wide range of (coating) applications.

Biocomposite structures are difficult to characterize by bulk approaches due to their morphological complexity and compositional heterogeneity. Therefore, a versatile method is required to assess, for example, the mechanical properties of geometrically simple parts of biocomposites at the relevant length scales. Here, it is demonstrated how a combination of Focused Ion Beam Scanning Electron Microscopy (FIB‐SEM) and micromanipulators can be used to isolate, transfer, and determine the mechanical properties of frustule constituents of diatom Thalassiosira pseudonana (T.p.). Specifically, two parts of the diatom frustule, girdle bands and valves, are separated by FIB milling and manipulated using a sharp tungsten tip without compromising their physical or chemical integrity. In situ mechanical studies on isolated girdle bands combined with Finite Element Method (FEM) simulations, enables the quantitative assessment of the Young's modulus of this biosilica; E = 40.0 GPa. In addition, the mechanical strength of isolated valves could be measured by transferring and mounting them on top of premilled holes in the sample support. This approach may be extended to any hierarchical biocomposite material, regardless of its chemical composition, to isolate, transfer, and investigate the mechanical properties of selected constituents or specific regions.