Boyko Tsyntsarski

Water contamination with surface-active agents, such as sodium lauryl sulfate (SLS), represents a serious environmental concern, driving the need for efficient and low-cost alternative adsorbents as a step toward sustainable waste valorization. In this study, waste biomass derived from plum stones, date stones, and walnut shells was successfully transformed into activated carbons via chemical activation using potassium hydroxide (KOH) at 850 °C with a 1:1 impregnation ratio. The synthesized materials underwent comprehensive physicochemical characterization utilizing TG-DSC, elemental analysis, Boehm titration, SEM, TEM, and nitrogen physisorption (BET), whereas their adsorption performance was evaluated against aqueous SLS solutions across various concentrations. The obtained results reveal a predominantly microporous structure with a high specific surface area, reaching up to 1059.01 m²/g for ACdate. The equilibrium adsorption data were well described by the Langmuir isotherm model, which yielded model-estimated asymptotic adsorption capacities (q_m) of 219.70 mg/g for ACwalnut, 178.25 mg/g for ACdate, and 57.80 mg/g for ACplum. These values represent Langmuir-derived model parameters rather than experimentally attained adsorption capacities within the investigated concentration range. Notably, despite having a lower specific surface area than ACdate, ACwalnut exhibited the highest Langmuir-estimated q_m, which may be associated with its structural balance and well-developed mesoporous network (0.210 cm³/g), facilitating the intraparticle transport of SLS molecules. These findings highlight that high efficiency originates from a synergistic combination of accessible porosity, a mesoporous transport network, hydrophobic character, and specific surface functional groups, demonstrating the exceptional potential of these activated carbons for anionic surfactant wastewater remediation.

Perfluoroalkyl and polyfluoroalkyl substances (PFASs) have become a global environmental concern due to their extreme persistence and toxicity. In this study, perfluorooctanoic acid (PFOA) was removed from aqueous solutions using porous carbon adsorbents synthesized from peach stones. The novelty of this work lies in the development of a procedure for obtaining a suitable carbon adsorbent, whose properties are consistent with the properties of the adsorbate. An appropriate activation was used, allowing the preparation of an adsorbent with a highly developed porous texture and a large surface area, which is a prerequisite for a significant adsorption capacity of the obtained adsorbents towards PFOA. Both carbon adsorbents obtained from peach pits, with clearly different surface chemistry—KOH-activated carbon (AC_KOH) and its nitric acid-oxidized derivative (AC_HNO3)—for PFOA adsorption were compared, along with the clarification of the relationship between the graphitic structure, pore development, surface functionality and adsorption characteristics. The first adsorbent was produced by chemical activation with KOH at 800 °C, while the second was obtained by oxidative modification of the activated sample with 12% HNO₃. Characterization by Raman spectroscopy, SEM, and nitrogen physisorption revealed a highly graphitized structure (ID/IG = 0.86) and well-developed porosity. Adsorption experiments were carried out at PFOA concentrations from 8 to 40 µmol/L using a spectrophotometric method based on methylene blue ion-pair extraction into chloroform. The results showed that AC_KOH exhibited a high maximum adsorption capacity of 1660 µmol/g (687.36 mg/g) and followed the Langmuir isotherm model, indicating monolayer adsorption. In contrast, AC_HNO3 showed a significantly lower adsorption capacity of 398.36 µmol/g (164.95 mg/g), which was attributed to electrostatic repulsion caused by acidic oxygen-containing surface groups. These findings demonstrate that peach stone-derived activated carbon is a promising, sustainable, and efficient adsorbent for the removal of PFOA from water.

Water purification by adsorption of various pollutants using carbon adsorbents with different characteristics has proven to be an effective method that is often used in purification technologies. In this work, a new method for obtaining a carbon adsorbent with a wide pore size and high surface area has been developed, particularly for the adsorption of bacterial cells. The characterization of the porous texture, the chemical nature of the surface, the structure, and the chemical composition of the obtained adsorbent is studied. The study demonstrates that the hierarchical macroporous structure of the macroporous carbon adsorbent (MCA) is highly effective for the physical sequestration of Escherichia coli from aqueous solutions. The high removal efficiency (86.4%) suggests that this material is a promising candidate for water purification and point-of-use filtration systems, where physical immobilization of pathogens is required.

This paper explores the complex interrelationships between biomass composition, thermochemical conversion pathways, carbon yield and other characteristics in order to expand the knowledge for biomass conversion processes and adapt them to specific requirements. A comprehensive characterization, chemical and thermal analysis of peach stone biomass, was performed. Thermogravimetric analysis, elemental analysis and low-temperature nitrogen sorption were also carried out in order to establish the composition and textural characteristics of the precursor material and obtained product. Carbon adsorbents were obtained from the studied biomass precursor under different conditions via one-step hydro-pyrolysis process by using steam activation at 800 °C. After research was conducted, it was established that cellulose is the main component, which influences the quantity and quality of the obtained adsorbent. The high content of hemicellulose reveals peach stones as a good candidate, especially for hydrothermal carbonization. High cellulose content (40%) in the biomass precursor is a prerequisite for the formation of porous texture in carbon adsorbent during hydro-pyrolysis. It was also shown that the carbon yield (26.70%) can be predicted and is highly dependent on the precursor composition. These results highlight the potential of peach stones as a valuable precursor for the production of sustainable, high-performance carbon adsorbents for environmental remediation.

Activated carbons were obtained from three types of raw materials from the canning industry: peach, plum, and olive stones. The chemical composition and texture of the precursors and the physicochemical properties of the obtained carbons were analyzed. It was found that under the same conditions of preparation, the properties of the raw materials significantly affect the parameters of the activated carbons. The obtained carbons were oxidized with 12% nitric acid to form a larger amount of acidic oxygen-containing groups on their surface. The porous texture, the size, and the chemical nature of the surface of the activated carbons were analyzed. The adsorption capacity of the obtained activated carbons towards chlorhexidine gluconate contained in mouthwash was determined. It was found that the three carbons have a significant adsorption capacity towards chlorhexidine gluconate: 189.1 mg/g for carbon from peach stones, 189.1 mg/g for carbon from plum stones, and 156.7 mg/g for carbon from olive stones, respectively. It has been determined that the adsorption of chlorhexidine gluconate on the surface of the obtained activated carbons obeys the Langmuir model. It has been established that the adsorption capacity of the obtained activated carbons is influenced by their porous texture, size, and chemical nature of the surface.

In this study two types of samples of spectrally pure graphite, compacted and coated with glassy carbon, were analyzed with liquid scintillation spectrometry, scanning electron microscopy (SEM) and X-ray diffractometry (XRD). “Space” sample has been sent in outer space on the surface of ISS for 28 months. “Space” sample is compared with “reference” sample, made of the same material, but stored on Earth for the same period. Radiation environment data were collected using R3DR2-Lyulin instrument, located in the outer space very close to the samples, in the same module of ISS. The effect of cosmic radiation leads to slight increase of ¹⁴C content, detected by liquid scintillation spectrometry. SEM and thermal test using XRD did not show any noticeable changes in terms of structure and phase composition. This confirms the high degree of reliability of this material under significantly milder operating conditions in Earth orbit.

The absorption of triclosan on the surface of four different carbon adsorbents, obtained on the base of plant and household waste (RDF), provided by Sofia Waste Plant, was investigated. The obtained results indicate that the most important parameters, which determine the process of triclosan adsorption by adsorbent surface are pore texture, the size of the accessible surface for the molecules of triclosan, and the chemical nature of the adsorbent surface. It was found that the obtained adsorbents can be successfully applied for the extraction of triclosan from waste and drinking water. The possibilities for solid products, obtained by thermal treatment of household and vegetable waste, to be applied successfully in a water purification technique are discussed.