Markus Grass

This study explores the potential of shearography for both in-process monitoring and structural health monitoring (SHM) of resistance spot welds. For in-process inspection, the method is applied immediately after the welding operation to monitor surface deformation during cooling, allowing a direct correlation between the measured deformation field and weld quality. For SHM applications, existing welds are thermally excited using induction, and their deformation response is analysed. The results demonstrate that shearography enables quantitative correlations between measured deformation gradients and mechanical weld properties such as nugget diameter. Furthermore, the integration of AI-based signal interpretation significantly enhances classification accuracy and robustness, paving the way for an automated, non-destructive 100 % inspection approach suitable for industrial implementation [15,16].

Climate change exacerbates the need for resource-efficient and cost-effective production processes across manifold industries, including the field of electrical connections. This specific field is characterized by a conflict of objectives, i.e., weight reductions while maintaining joint strength and electrical conductivity. From a material point of view, the use of aluminum as a conductor material is suitable for this application, as it is lighter than copper, a classical conductor material. Electrical conductors are often used in the form of flexible cables, so-called stranded wires. This type of conductor as well as the fact that the sole use of aluminum in electrical systems is not feasible, e.g., because the predetermined connection terminals of power electronic components are made of copper, creates a substantial demand for dissimilar aluminum-copper cable arrester joints. However, traditional fusion-based welding processes have proved incapable of reliably producing these dissimilar aluminum-copper joints because of thermophysical effects and chemical incompatibilities, the latter eventually leading to the formation of intermetallic phases. These phases adversely affect the quality of the joint in terms of both mechanical and electrical performance. Yet, magnetic pulse welding, a pressure welding process, is ideally suited for producing dissimilar metal joints on the basis of a low energy input during the welding process. Consequently, the formation of intermetallic phases is restrained. However, magnetic pulse welding has not been sufficiently investigated for the reliable contacting of stranded cables to tubular arresters. As a result, this paper focuses on the fabrication of tubular stranded cable arrester joints using magnetic pulse welding. To shed light on possible material combinations, aluminum-to-aluminum and copper-to-copper joints as well as their dissimilar counterparts are welded. Subsequently, the joints are characterized with regard to their microstructure and quasi-static material strength. Electrical characterization comprises the four-wire Kelvin measurement method to evaluate the resistance of the electrical joints. The results demonstrate that magnetic pulse welding is ideally suited to join the aforementioned material combination and joint configuration due to its process characteristics eventually leading to material continuity. As a result, the stranded wires are welded to the tubular arresters rather than crimped. Consequently, a comparative analysis of the joint properties with those of the joining partners shows that the measured electrical resistances and mechanical tensile forces may be considered very good.

Climate change exacerbates the need for resource-efficient and cost-effective production processes across manifold industries, including the field of electrical connections. This specific field is characterized by a conflict of objectives, i.e., weight reductions while maintaining joint strength and electrical conductivity. From a materials point of view, the use of aluminum as a conductor material is suitable for this application, as it is lighter than copper, a classical conductor material. Electrical conductors are often used in the form of flexible cables, so-called stranded wires. This type of conductor as well as the fact that the sole use of aluminum in electrical systems not feasible, e.g., because the predetermined connection terminals of power electronic components are made of copper, creates a substantial demand for dissimilar aluminum-copper cable arrester joints. However, traditional fusion-based welding processes have proved incapable of reliably producing these dissimilar aluminum-copper joints because of thermophysical effects and chemical incompabilities, the latter eventually leading to the formation of intermetallic phases. These phases adversely affect the quality of the joint in terms of both mechanical and electrical performance. Yet, magnetic pulse welding, a pressure welding process, is ideally suited for producing dissimilar metal joints on basis of a low energy input during the welding process. Consequently, the formation of intermetallic phases is restrained. However, magnetic pulse welding has not been sufficiently investigated for the reliable contacting of stranded cables to tubular arresters. As a result, this paper focuses on the fabrication of tubular stranded cable arrester joints using magnetic pulse welding. To shed light on possible material combinations, aluminum to aluminum and copper to copper joints as well as their dissimilar counterparts are welded. Subsequently, the joints are characterized with regard to their microstructure and quasi-static material strength. Electrical characterization comprises the four-wire Kelvin measurement method to evaluate the resistance of the electrical joints. The results demonstrate that magnetic pulse welding is ideally suited to join the aforementioned material combination and joint configuration due to its process characteristics eventually leading to material continuity. As a result, the stranded wires are welded to the tubular arresters rather than crimped. Consequently, a comparative analysis of the joint properties with those of the joining partners shows that the measured electrical resistances and mechanical tensile forces may be considered very good.

In this paper, the potential of directional ultrasonic wave superposition by moving sound generators for laser beam welding of high-strength steel alloys 1.5528 (22MnB5) is studied. Steel sheets of identical thickness and in form of tailored blanks were joined in butt joint configuration. The influences of the various excitation parameters of the moving sound generators on the ultrasonic coupling and their influence on the distribution of the AlSi coating components within the melting zone and the weld seam characteristics are investigated. Etched cross-sections, scanning electron microscopy, energy dispersive X-ray spectroscopy, and electron backscattering measurements were used as the investigation methods to determine the AlSi distribution in the weld as well as its microstructure. The results presented a series of experiments which show that a suitable superposition of ultrasonic waves by the moving sound generators lead to a more homogeneous distribution of AlSi particles in the melt as well as to a finer microstructure within the weld, which improves the mechanical–technological properties.

The present study provides an overview of previous studies on the welding of the AA7075-T6 aluminum alloy, followed by an investigation of the influence of short-time solution annealing on the mechanical properties of the weld. Conventional laser welding of Al-Zn-alloys leads to a low weld strength, which makes a post weld heat treatment (PWHT) favorable. The PWHT includes solution annealing, quenching and subsequent aging. For solution annealing, different holding times and cooling rates are investigated in this study. The focus of the investigation is on a short solution annealing time, which on the one hand is ecological and economically favorable and on the other hand offers great potential for inline heat treatments. The shortest solution annealing time of 10 s shows a significant increase in weld strength (joint efficiency of 72%), compared to the non-heat treated weld (joint efficiency of 52%). The microstructural analysis reveals that the cooling rate after solution heat treatment affects the formation of precipitates in the microstructure of the welded AA7075 alloy. Moreover, the enhancement of mechanical properties is related to the formation of Mg-Al-Cu and Mg-Zn rich precipitates.