Bin Jiang

As a natural building material, rammed earth has gained significant attention due to its environmental friendliness, low cost, and sustainability. This study conducted a dynamic simulation of heat and moisture transfer in rammed earth and brick buildings to compare their energy performance under identical conditions. The results indicated that the annual minimum indoor temperature in rammed earth buildings was 0.7 °C higher, while the maximum was 0.4 °C lower than that in brick buildings. The minimum and maximum indoor relative humidities were 11.4% higher and 9.6% lower, respectively, in rammed earth buildings, with an annual average of 69.2%, which is slightly lower than that of brick buildings. The annual heating and cooling energy consumption in brick buildings was 1.37 and 1.2 times greater, respectively, than in rammed earth buildings, and their monthly dehumidification demands were consistently higher. The effect of wall thickness on energy consumption revealed that increasing the thickness from 200 to 250 mm reduced energy use by 9.3%, whereas an increase from 450 to 500 mm yielded a 4.2% reduction. When the wall thickness exceeded 400 mm, the energy savings were marginal (<5%), whereas the construction costs and space occupancy increased. Therefore, a wall thickness of 350–400 mm is recommended to optimize the trade-off between energy efficiency, thermal-moisture performance, and cost-effectiveness.

Rammed-earth dwellings have a long history in the construction field. It is a natural material that is both green and environmentally friendly. In recent years, the advantages of rammed earth, such as environmental protection, low cost, and recyclability, have attracted considerable attention. In this study, the thermal and humidity physical properties of rammed–earth materials in the northwest Sichuan region, the variation laws of thermal physical parameters, such as the thermal conductivity of rammed–earth under different moisture content conditions, and isothermal moisture absorption and desorption curves were investigated. The results indicated that the thermal physical parameters of the rammed earth measured in the experiment increased with an increase in moisture content, and its moisture absorption performance was better than the moisture release performance in the range of 11.31–97.3% relative humidity. The experimental site, Mianyang City, Sichuan Province, is a subtropical monsoon humid climate zone characterized by warm winters and hot summers with four distinct seasons. In this study, we investigated the hygrothermal coupling transfer of walls, as well as the indoor temperature and humidity changes in new rammed–earth buildings during summer and winter climates. During the test period, the maximum indoor temperature in summer was 35.08 °C, the minimum temperature was 33.76 °C, and the average daily temperature fluctuation was 3.62 °C. In winter, the maximum indoor temperature was 8.59 °C, the minimum temperature was 6.18 °C, and the average daily temperature fluctuation was 1.21 °C. An analysis was performed on the thermal insulation performance of rammed–earth buildings in an extremely high-temperature climate during summer, thermal insulation performance, the thermal–buffering capacity of walls in a low–temperature and high-humidity climate during winter, and thermal and humidity regulation of indoor environments provided by walls during summer and winter. The results showed that the rammed–earth buildings exhibited warmth in winter, coolness in summer, and a more stable and comfortable indoor environment.

As environment-friendly building materials, earth materials are attracting significant attention because of their favorable hygrothermal properties. In this study, the earth materials in northwest Sichuan were tested and curves of thermal conductivity and water vapor permeability with relative humidity were obtained. The function curves and constants of the two coefficients were substituted into the verified nonstationary model of heat and moisture transfer in rammed earth walls and indoor air for calculation. The difference in the calculation results when the hygrothermal parameters are functions and constants were analyzed, and the influence of the non-constant hygrothermal parameters on the heat and moisture transfer in rammed earth walls, was obtained. The test results show that thermal conductivity is linearly related to moisture content, and water vapor permeability has a small variation in the relative humidity range of 0–60% and increases exponentially above 60%. The calculation results indicate that the non-constant hygrothermal parameters have little influence on the internal surface temperature of the rammed earth walls and Mianyang City’s indoor air temperature and humidity during the summer and winter. The heat transfer on the internal surface will be underestimated by using a non-constant for the hygrothermal parameter when the moisture content of the wall is low, and vice versa. In hot-humid areas or seasons with large differences in temperature and humidity between indoors and outdoors, non-constant hygrothermal parameters have a more obvious effect on heat transfer on the internal surface of the wall. The results of this study demonstrate the necessity of parameter testing.

The climate crisis is one of the most important problems today. In the process of human building, the use of cement, steel, and other industrial materials in the process of building construction and recycling has brought a huge burden to the natural environment. Earth is one of the oldest building materials, its availability and insulation make it an excellent constructive solution in human history. Among several existing earth construction techniques, rammed earth is one of the most relevant. In this paper, a numerical model of the rammed earth folk house in Mianyang was established, and an experimental device was built to verify it. With the typical meteorological year data of Mianyang in northwest Sichuan, the heat and moisture transfer in rammed earth wall, as well as the indoor thermal and moisture environment were numerically simulated. The results show that the rammed earth wall weakens the temperature fluctuation of the inner surface of the wall and makes the peak temperature of the inner surface of the wall lag the outer surface. The relative humidity in the center of the rammed earth wall can be maintained at about 60%, both in winter and summer. The moisture absorption and desorption capacity of rammed earth walls without inner decorative materials is about three times that of gypsum board, and the use of a waterproof coating will render the rammed earth wall almost unable to adjust the indoor relative humidity. Additionally, the use of decorative materials will increase the fluctuation range of indoor relative humidity and the risk of mold breeding.

As a traditional building material, rammed earth has gained popularity for its environmental friendliness and reusability. In this study, the hygrothermal performance of the wall material of traditional rammed-earth dwellings was experimentally measured, and the indoor and outdoor temperature and humidity variations of rammed-earth dwellings were experimentally measured for five days. Considering temperature and relative humidity as the driving potential for heat and humidity transfer and air penetration, an unsteady model of heat and humidity transfer of the rammed-earth wall and indoor and outdoor air was established. The accuracy of the model was verified using the measured data. The model was used to determine the rationality of the wall thickness in local rammed-earth dwellings. Based on data from typical local meteorological years, the indoor temperature and humidity changes in rammed-earth dwellings were numerically predicted. The average indoor temperature and humidity in summer were 26.56°C and 69.74%, and the variances were 3.26 and 43.17, respectively. The average indoor temperature and humidity in winter were 7.25°C and 83.62%, and the variances were 1.14 and 14.83, respectively. The research results demonstrate that a rammed-earth wall significantly reduces the influence of outdoor temperature fluctuation on the indoor thermal environment, with good humidity regulating performance.