With the rapid development of modern electrical and electronic applications, the demand for high-performance film capacitors is becoming increasingly urgent. The energy density of a capacitor is dependent on permittivity and breakdown strength. However, the development of polymer-based composites with both high permittivity (ε_r) and breakdown strength (E_b) remains a huge challenge. In this work, a strategy of doping synergistic dual-fillers with complementary functionalities into polymer is demonstrated, by which high ε_r and E_b are obtained simultaneously. Small-sized titania nanosheets (STNSs) with high ε_r and high-insulating boron nitride sheets coated with polydopamine on the surface (BN@PDA) were introduced into poly(vinylidene fluoride) (PVDF) to prepare a ternary composite. Remarkably, a PVDF-based composite with 1 wt% BN@PDA and 0.5 wt% STNSs (1 wt% PVDF/BN@PDA−STNSs) shows an excellent energy storage performance, including a high ε_r of ~13.9 at 1 Hz, a superior E_b of ~440 kV/mm, and a high discharged energy density U_e of ~12.1 J/cm³. Moreover, the simulation results confirm that BN@PDA sheets improve breakdown strength and STNSs boost polarization, which is consistent with the experimental results. This contribution provides a new design paradigm for energy storage dielectrics.

With the wide application of energy storage equipment in modern electronic and electrical systems, developing polymer-based dielectric capacitors with high-power density and rapid charge and discharge capabilities has become important. However, there are significant challenges in synergistic optimization of conventional polymer-based composites, specifically in terms of their breakdown and dielectric properties. As the basis of dielectrics, all-organic polymers have become a research hotspot in recent years, showing broad development prospects in the fields of dielectric and energy storage. This paper reviews the research progress of all-organic polymer dielectrics from the perspective of material preparation methods, with emphasis on strategies that enhance both dielectric and energy storage performance. By dividing all-organic polymer dielectrics into linear polymer dielectrics and nonlinear polymer dielectrics, the paper describes the effects of three structures (blending, filling, and multilayer) on the dielectric and energy storage properties of all-organic polymer dielectrics. Based on the above research progress, the energy storage applications of all-organic dielectrics are summarized and their prospects discussed.