Yulong Ma

The interface performance of steel fiber-reinforced concrete (SFRC) is a critical factor in determining mechanical properties and durability. The degradation of the concrete matrix and micro-structure interface is caused by environmental erosion, which shortens the service life of the structure design. Considering different volume contents of steel fiber (0%, 1%, 2%), the failure mechanism of SFRC under different environmental erosion conditions was studied through a laboratory test scheme. A total of six environmental factors are selected, including water, sodium chloride solution, sodium sulfate solution, dilute sulfuric acid solution, sodium hydroxide solution, and a freeze-thaw cycle. When subjected to different erosion concentrations and periods, micro-structure and axial bearing capacity deterioration laws are compared and analyzed. A durability equation related to fiber mixture ratio and strength is presented based on the experimental data and the numerical simulation method. The influence of different environments on steel fiber-reinforced concrete is analyzed, and the grey correlation degree of axial compressive strength is analyzed. The experimental results show that steel fiber can effectively improve the concrete axial bearing capacity, but different responses are observed under the various erosion conditions. A freeze-thaw cycle environment has the most significant impact on the axial compressive strength of concrete, followed by the sulfuric acid environment, and other environments have a weaker impact. The research results will provide a theoretical basis for predicting the performance deterioration of SFRC concerning other erosion conditions and periods.

Fibers used as reinforcement can increase the mechanical characteristics of engineering cementitious composites (ECC), but their frost resistance has received less attention. The mechanical properties of various fiber cementitious materials under the dual factors of freeze-thaw action and fiber dose are yet to be determined. This study examines the performance change patterns of cementitious composites, which contain carbon fiber, glass fiber, and polyvinyl alcohol (PVA) fiber at 0%, 0.5%, and 1% volume admixture in freeze-thaw tests. Three fiber cement-based materials are selected to do the compression and bending testing, and ABAQUS finite element modeling is used to assess the performance of fiber cement-based composite materials. The microscopic observation results show that the dispersion of glass and PVA fibers is higher than that of carbon fibers. As a result, the mechanical characteristics of the fiber-doped cementitious composites increase dramatically after freeze-thaw with increasing dosage. The compression test results show the frost resistance of carbon fiber > PVA fiber > glass fiber. In addition, the bending test results show the frost resistance of carbon fiber > glass fiber > PVA fiber. The 3D surface plots of the strength changes are established to observe the mechanical property changes under the coupling effect of admixture and freeze-thaw times. ABAQUS modeling is used to predict the strength of the cementitious composites under various admixtures and freeze-thaw cycles. The bending strength numerical equation is presented, and the bending and compressive strengths of three different fiber-cement matrix materials are accurately predicted.