Bolin Wang

Three-dimensional concrete printing (3DCP) technology with solid wastes has significant potential for sustainable construction. However, the hardened mechanical properties of components manufactured using 3DCP technology are affected by weak interlayer interfaces, limiting the widespread application of 3DCP technology. To address the inherent limitations of 3DCP technology, conventional improvement strategies, such as external reinforcement and the optimization of material properties, lead to increased production costs, complex fabrication, and decreased automation. This study proposes an innovative spatial path optimization method to enhance the mechanical performance of 3D-printed, cement-based components. The novel S-path design introduces additional printed layers in the weak interlayer regions of the printed samples. This design improves the spatial distribution of fiber-reinforced filaments in continuous weak zones, thus enhancing the functional efficiency of fibers. This approach improves the mechanical performance of the printed samples, achieving compressive strengths close to those of cast samples and only a 20% reduction in average flexural strength. Compared to using a conventional printing path, the average compressive strength and flexural strength are improved by 30% and 55%, respectively, when the S-path layout is employed in 3DCP. Additionally, this method significantly reduces the anisotropy in compressive and flexural strengths to 26% and 28% of samples using conventional printing paths, respectively. Therefore, the proposed method can improve the mechanical properties and stability of the material, reducing the safety risks of printed structures.

Three-dimensional (3D) concrete printing (3DCP) technology attracts significant attention from research and industry. Moreover, adequate mechanical performance is one of the primary properties for materials, meeting the demand of structural safety using 3DCP technology. However, research on curing conditions as the significant influence factor of mechanical capacity is required to accelerate the practical application of 3DCP technology. This study aims to explore the impact of various steam curing conditions (heating rate, constant temperature time, and constant temperature) on the mechanical performance of printed concrete containing solid wastes. Moreover, the optimal steam curing conditions are obtained for compressive, tensile, and flexural properties in different directions. Subsequently, anisotropies in the mechanical properties of printed composites and interlayer bonding behaviors are investigated when various curing conditions are employed. The result shows that steam curing conditions and solid waste incorporation improves the interlayer bond for 3D printed cement-based composites.

Three-dimensional concrete printing is a promising technology and attracts the significant attention of research and industry. However, printable and mechanical capacities are required for 3D printable cementitious materials. Moreover, the quantitative analysis methods of printable performance are limited and have low sensitivity. In this study, the orthogonal experiment through samples combining 3D concrete printing method with fly ash, silica fume, and ground granulated blast furnace slag was designed to obtain the printable and mechanical property influence of various mix proportions. Furthermore, multiple industrial wastes were utilized to improve material sustainability. Meanwhile, the static and dynamic extrusion pressure measured by the original 3D printing extrudability tester were verified to achieve a high-sensitivity evaluating indicator. Thereby, a novel high-sensitivity quantitative analysis method of printable capacity was established to explore the influence of industrial wastes usage on the printability of 3D printable mortars. The optimum dosage of fly ash, silica fume, and ground granulated blast furnace slag was 20 wt.%, 15 wt.%, and 10 wt.%, respectively, based on printable and mechanical property experiments. Furthermore, the optimum dosage was employed to print the sample and achieved a higher compressive strength (56.3 MPa) than the control cast.