Moad Alosta

Portland cement (PC) is a common material used in civil infrastructure engineering. Cement production emits roughly 2.2 billion tons of CO₂ per year, contributing 8% of global emissions in 2016. This contributes to almost half of the calcination process, and together with thermal combustion, clinker generation could be responsible for 90% of the sector’s emissions. One effective technique for dealing with these industrial by-product wastes is to employ them to make cement replacements such as concrete and mortar, which can be used in a variety of applications. As a result, the purpose of this research is to review the current advancements, challenges, and future perspectives on the utilization of agro-industrial waste (AIW) produced around the world in cement-based products. Geopolymers (GPs), on the other hand, reduce carbon dioxide emissions and have the potential to be a complete or partial replacement for PC in the construction sector. The GP technology enables the use of AIW in combination with an alumina–silicate (A–S) phase with minimal environmental impact. GP-cement is mostly produced by activating alkali silicates or alkali sols with secondary raw materials such as calcined clays, fly ash (FA), zeolite, metakaolin, etc. Mixing various resource materials, including additives, A–S, and alkali sols, alkali concentrations, optimizing the curing temperature, the SiO₂/Na₂O ratio, microstructural behavior, and other factors, results in GP-cement with outstanding mechanical and durability characteristics. The review concludes that AIW-based geopolymer composites have shown promising results in terms of their mechanical properties, durability, and environmental sustainability, which makes them emerge as promising future building materials with applications in a wide range of industries.

This study focused on identifying the most appropriate structural system for multi-story buildings and analyzing its response to lateral loads. The study analyzed and compared the different structural systems to determine the most suitable option. The study aims to utilize three lateral framing systems (moment, braced, and diagrid) in order to investigate which system needs the least amount of steel to meet the design requirements. Thus, in order to determine the estimated steel savings of this system as compared to the moment and braced frames, the four-story and eight-story buildings that are 96′ × 96′ in the plane and utilize moment frames, braced frame, and diagrid framing structural systems are presented. Based on the American Society of Civil Engineers (ASCE) 7–10, load combinations are considered for the designs, and the RAM structural analysis is used for the modeling and analysis of the structural systems. The findings of this study’s illustrations were the optimum for the analysis of wind of 176 kips and seismic loads of 122 kips, the building’s lateral displacements, which were the lowest at 0.045 inches, the story drift, the story stiffness, and the story shear for each structural system. In addition, the diagrid system also had the least amount of shear for all the stories, suggesting that it is better able to manage the lateral forces. These results indicate that the diagrid system is a more efficient structural system and can be recommended for use in multi-story buildings.

The safe disposal of an enormous amount of waste glass (WG) in several countries has become a severe environmental issue. In contrast, concrete production consumes a large amount of natural resources and contributes to environmental greenhouse gas emissions. It is widely known that many kinds of waste may be utilized rather than raw materials in the field of construction materials. However, for the wide use of waste in building construction, it is necessary to ensure that the characteristics of the resulting building materials are appropriate. Recycled glass waste is one of the most attractive waste materials that can be used to create sustainable concrete compounds. Therefore, researchers focus on the production of concrete and cement mortar by utilizing waste glass as an aggregate or as a pozzolanic material. In this article, the literature discussing the use of recycled glass waste in concrete as a partial or complete replacement for aggregates has been reviewed by focusing on the effect of recycled glass waste on the fresh and mechanical properties of concrete.

There is currently an increasing demand for Building Information Modelling (BIM) to be integrated into green projects. BIM is able to evaluate green building assessment tools by digitising and assessing buildings during their development stage. In Malaysia, the Green Building Index (GBI) promotes sustainability in the built environment. Six categories of criteria will be assessed in three of the certification stages. This study focuses on how BIM applications can digitise the GBI criteria for GBI processes. It examines BIM uses and tools of each GBI credit and defines the responsibility and role of construction stakeholders in using BIM to examine the assessment methods used for new non-residential building construction based on GBI. The primary method for data collection is the focus group interview which involves the groups of stakeholders involved in a BIM and GBI project. The result of the BIM–GBI assessment method showed that BIM could digitise and assess 25 credits in Design Assessment (DA), which can achieve 55 points of the total 100 points. This study helps stakeholders define the design team and facility manager’s roles to obtain GBI certification and maintain the certification during the building’s operation stage.

Push‐out‐shear tests were used in this study to analyze lag screw connections in timber‐concrete composite (TCC) slabs based on the embedment depth. The goal of this research is to look into the relationship between shear capacity and embedment depth in TCC, as well as to investigate the embedment strength of the wood. Experiments were carried out at different embedment depths (5.08 cm, 7.0 cm, and 8.9 cm). The prepared samples were examined in order to determine the failure modes and provide an accurate assessment of the influence of embedment depth on TCC slabs. The investigation on the embedment strength of the wood was performed then for the analysis of the crushing of wood fibers, lag screw yielding strength, and maximum load applied at embedment depths of 6.6 cm and 7.0 cm. The results indicate that between 5.08 cm and 7.0 cm, there was an apparent improvement in the relationship between embedment depth (ED) and shear capacity of TCC slabs in terms of the shear strength, while a significant difference was observed between 7.0 cm and 8.9 cm. The study suggests that the ED of the TCC slab should be maintained at around 7.33 times the diameter of the lag screw.