Silver nanoparticles (AgNPs) are widely recognized as a prominent antimicrobial agent and have found applications in the field of medicine. This study focuses on the synthesis of AgNPs utilizing the natural reducing agent of Ceylon olive (Elaeocarpus serratus), presenting an economically viable and ecologically friendly approach. For the first time, this research demonstrated the synthesis of AgNPs using phytochemicals extracted from Ceylon olive, serving as both natural reducing and stabilizing agents. The synthesized AgNPs were characterized with UV–visible spectroscopy, a particle size analyzer (PSA), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM) coupled with an energy dispersive X-ray spectrometer (EDX). The UV–visible spectra primarily indicated the formation of the AgNPs by the surface plasmon resonance band around 434 nm. SEM analysis confirmed the presence of silver nanoparticles within a size range of 50–110 nm, with an average size of approximately 70 nm. FTIR determined that proteins, phenols, and flavonoids may have acted as reducing and capping agents. Experimental parameters were optimized to improve the yield and size of the AgNPs and eventually evaluate their antibacterial properties. The well diffusion method exhibits a significantly larger zone of inhibition for Gram-negative bacterial strains (18.4 ± 0.55 mm for Pseudomonas aeruginosa and 14.4 ± 0.55 mm for Escherichia coli) compared to Gram-positive bacterial strains (11.6 ± 0.55 mm for Staphylococcus aureus and 10.4 ± 0.55 mm for Staphylococcus epidermidis) for 50 µg/mL AgNPs. These findings demonstrate that AgNPs synthesized with Ceylon olive have the potential to develop into novel materials for bacterial-mediated diseases.

Solid Oxide Cells (SOC) are the kind of electrochemical devices that provide reversible, dual mode operation, where electricity is generated in a fuel cell mode and fuel is produced in an electrolysis mode. Our current work encompasses the design, fabrication, and performance analysis of a micro-tubular reversible SOC that is prepared through a single dip-coating technique with multiple dips using conventional materials. Electrochemical impedance and current-voltage responses were monitored from 700 to 800 °C. Maximum power densities of the cell achieved at 800, 750, and 700 °C, was 690, 546, and 418 mW cm⁻², respectively. The reversible, dual mode operation of the SOC was evaluated by operating the cell using 50% H₂O/H₂ and ambient air. Accordingly, when the SOC was operated in the electrolysis mode at 1.3 V (the thermo-neutral voltage for steam electrolysis), current densities of −311, −487 and −684 mA cm⁻² at 700, 750 and 800 °C, respectively, were observed. Hydrogen production rate was determined based on the current developed in the cell during the electrolysis operation. The stability of the cell was further evaluated by performing multiple transitions between fuel cell mode and electrolysis mode at 700 °C for a period of 500 h. In the stability test, the cell current decreased from 353 mA cm⁻² to 243 mA cm⁻² in the fuel cell mode operation at 0.7 V, while the same decreased from −250 mA cm⁻² to −115 mA cm⁻² in the electrolysis operation at 1.3 V.