Riboflavin derivatives enable sustainable, light-driven synthesis of polymer brushes via organocatalyzed ATRP under mild conditions with a simple reaction setup.

The unique features of poly[2‐(dimethylamino)ethyl methacrylate] (PDMAEMA), such as its sensitivity to external stimuli like pH and the presence of tertiary amine groups that can be easily quaternized to introduce antibacterial properties, make it a promising platform for biomedical applications. In this contribution, a facile, cost‐effective, and ecological procedure for controlled grafting of PDMAEMA brushes from a glass surface, both in mL and µL scale, is developed. This concept involves utilizing an aqueous solution of sunflower honey as a source of reducing sugars to accelerate surface‐initiated activators regenerated by electron transfer atom transfer radical polymerization. The PDMAEMA chains covalently grafted to the glass surface are then quaternized to form an antibacterial film. The thickness of the polymeric brush layer is determined by atomic force microscopy, while the chemical composition is analyzed by time of flight secondary ion mass spectrometry. Water contact angle measurements demonstrate the pH‐sensitivity of PDMAEMA pointing out the potential application of the prepared material as smart surfaces. Furthermore, the antibacterial tests against Gram‐positive and Gram‐negative bacteria strains are performed. The protein adsorption is used to evaluate the biocompatibility of the prepared surfaces. The resulting glass materials can serve as multifunctional surfaces for various purposes.

The high stability and conductivity of 3,4-disubstituted polythiophenes such as poly(3,4-ethylenedioxythiophene) (PEDOT) make them attractive candidates for commercial applications. However, next-generation nanoelectronic devices require novel macromolecular strategies for the precise synthesis of advanced polymer structures as well as their arrangement. In this report, we present a synthetic route to make ladder-like polymer brushes with poly(3,4-propylenedioxythiophene) (PProDOT)-conjugated chains. The brushes were prepared via a self-templating surface-initiated technique (ST-SIP) that combines the surface-initiated atom transfer radical polymerization (SI-ATRP) of bifunctional ProDOT-based monomers and subsequent oxidative polymerization of the pendant ProDOT groups in the parent brushes. The brushes prepared in this way were characterized by grazing-angle FTIR, XPS spectroscopy, and AFM. Steady-state and time-resolved photoluminescence measurements were used to extract the information about the structure and effective conjugation length of PProDOT-based chains. Stability tests performed in ambient conditions and under exposure to standardized solar light revealed the remarkable stability of the obtained materials.