Il-Ho Na

Although asphalt mixtures can be applied to railway tracks due to their viscoelastic properties, caution is required, as their ductility and brittleness are highly sensitive to temperature variations. In recent years, interest in the application of asphalt in railway infrastructure has increased, driven by the development of modified mixtures and the broader availability of performance-enhancing additives. Additionally, evaluation methods for railway tracks should be adapted to account for the distinct loading mechanisms involved, which differ from those of conventional roadways. In this study, the comprehensive properties of asphalt binders, mixtures, and testing methods—including physical and engineering characteristics—were assessed to improve the performance of asphalt concrete layers for potential applications in railroad infrastructure. The results of this study indicate that (1) the higher the performance grade (PG), the higher the indirect tensile strength (ITS) value achieved by the 13 mm mixture using PG76-22, which is higher than that of the PG64-22 mixture. This indicates that higher PG grades and modification contribute to improved tensile strength, beneficial for upper layers subjected to dynamic railroad loads. (2) The tensile strength ratio (TSR) increased from the unmodified mixture to over 92% in mixtures containing crumb rubber modifier (CRM) and styrenic thermoplastic elastomer (STE), demonstrating enhanced durability under freeze–thaw conditions. (3) Wheel tracking test results showed that modified mixtures exhibited more than twice the rutting resistance compared to PG64-22. The 13 mm aggregate mixtures also generally performed better than the 19 mm mixtures, indicating reduced permanent deformation under repeated loading. (4) It was concluded that asphalt is a suitable material for railroads, as its overall characteristics comply with standard specifications.

Various environmentally friendly additives have been used to mitigate significant damage, such as plastic deformation and cracking, in asphalt pavements over the long term. Despite the existence of research demonstrating the efficacy of the materials for asphalt mixture, there has been a lack of studies focusing on the recycling of modified asphalt binders. Therefore, this study conveys the laboratory evaluation of the high-temperature properties of 12 recycled polymer-modified asphalt (PMA) binders as basic research. The data evaluation was carried out using crumb rubber modifier (CRM), styrene-butadiene-styrene (SBS), and styrene-isoprene-styrene (SIS) modified binders, depending on their recycled binders. To assess the properties of each binder, the viscosity and viscoelasticity were measured. Overall, the results of this study revealed that (1) an increasing trend for the viscosity of all asphalt binders was seen as the recycled binder was added and showed their characteristics depending on modifiers; (2) the tendency for using each modified binder in the original and rolling thin-film oven (RTFO) condition appeared for modifiers to have their properties when reusing them; (3) from the J_nr and %rec values, each property of modifiers kept its inherent characteristics, but a potential limit was seen in that a styrene block copolymer was mainly effective on this test method. To sum up, modifiers in asphalt mixture can have their unique properties even after reusing them in recycled asphalt mixture. Therefore, it is recommended that modifiers in asphalt mixture are considered as a potential factor in utilizing reclaimed asphalt pavement (RAP).

Demand for various bicycles and sharing systems has constantly been growing worldwide as they improve the quality of life and promote eco-friendly transportation. Accordingly, it is inevitable that bicycle roads should be expanded. As bicycle roads have a relatively lower load applied than automobile roads, adopting a design method that uses a high reclaimed asphalt pavement (RAP) content can be beneficial. However, much uncertainty still exists about the relation between the mixing method and application in field sites, without appropriately considering the quality control of the rejuvenator. Therefore, this study aims to demonstrate the effect of base oil as a rejuvenator on aged binders, considering the use of a high RAP content for bicycle roads. To prepare the aged binder, a rolling thin-film oven (RTFO) and pressure aging vessel (PAV) were used to imitate the life cycle of asphalt pavement from production to service life, and then three contents of aged binder (0%, 50%, and 100%) were added and mixed with fresh PG 64-22 base binder. Finally, each type of prepared aged asphalt binder was blended with three different base oil contents (0%, 5%, and 10%). The results indicated that (1) the addition of base oil effectively decreased the viscosity of aged binders, (2) aged binders containing base oil showed less G*/sin δ compared to originally aged binders, and (3) the application of base oil improves the cracking properties of the aged binder by decreasing stiffness. In conclusion, the most striking observation from the data analysis from the Superpave test and statistical results was the effect of reducing the asphaltene portion based on the use of base oil in the aged binder. Therefore, using base oil in RAP can enable the application of a high RAP content to the bicycle road.

Crumb rubber binder with thermoplastic polyurethane (TPU) has been experimented with to characterize the performance properties considering the workability, rutting, fatigue cracking and cracking resistance at low temperatures depending on the temperatures and aging states. Physical and rheological properties were evaluated to proceed with the study by applying Superpave asphalt binder testing and multi-stress creep recovery (MSCR). Based on the targeted experiments, the binder samples were produced at three aging states (original, short-term aged and long-term aged) using a rolling thin film oven (RTFO) and pressure aging vessel (PAV). The results revealed that (i) the addition of TPU into CRM binders has a potential effect on increasing viscoelasticity at the original condition, (ii) CRM binders containing TPU showed improved anti-aging performance based on results of RTFO residues and (iii) the inclusion of TPU made it possible for CRM asphalt binder to improve its fatigue and cracking resistance at low temperature.