Daniel Baier

Wire and Arc Additive Manufacturing (WAAM) of Ti-6Al-4V is becoming increasingly important in the aerospace industry for the production of large parts. Due to the high welding requirements of the material, high quality demands are placed on the process. To meet these high demands, quality assurance measures are applied to maintain mechanical and geometrical part properties. First, the interlayer temperatures that are applied influence the final geometry. The part must meet geometric accuracies in order to be machined after the WAAM process. Second, Ti-6Al-4V materials have a high affinity to absorb oxygen from the environment at elevated temperatures. This oxygen uptake results in a discoloration of the surface and an embrittlement of the material. Therefore, a defined and monitored oxygen content in the build chamber is crucial. This work presents an approach to determine limitations for the interlayer temperature of the part and the oxygen content in the build chamber. The influence of a temperature deviating from the set interlayer temperature on the layer width was analyzed. By varying the interlayer temperature, the layer width varied by up to 3 mm. It was shown that different restrictions for the oxygen content in the build chamber apply depending on the part size.

The Wire and Arc Additive Manufacturing (WAAM) process has a high potential for industrial applications in aviation. The interlayer temperatures influence the dimensions and geometric deviations of the part. Monitoring the absolute interlayer temperature values is necessary for quantifying these influences. This paper presents an approach for determining the absolute values of the interlayer temperatures during the process using Ti-6Al-4V. The emissivity and transmittance are determined and calibrated, enabling precise thermographic measuring during the WAAM process. The recorded thermographic data are then compared to signals of thermocouples so that the absolute temperature values can be aligned. The methodology is validated by its transfer to measure the interlayer temperature at different regions of interest. The effect of a heat accumulation using Ti-6Al-4V in WAAM was determined. The methodology enables a reproducible and non-tactile measurement of the interlayer temperature during the WAAM process. The results show that with an interlayer temperature of 200 °C, a heat accumulation occurs within a layer. The heat accumulates in the center of the layer because the free ends of the layer cool down faster than the center of the layer.

Wire and Arc Additive Manufacturing (WAAM) is a promising technology for the fabrication of large metal parts. During the process, the wire electrode is melted continuously or in a pulsating mode and deposited layer-by-layer onto a substrate. Due to the recurring energy input into the part during WAAM, adequate thermal management is crucial. The temperature distribution, especially the interlayer temperature in the part, is determined by the parameter settings as well as by the dwell times and can be monitored. This paper presents the cause-effect relationships between the interlayer temperature and the dwell times to enable a suitable temperature management. Thermal imaging was implemented during the manufacturing process, allowing the analysis of different interlayer dwell times and their effect on the interlayer temperatures. In addition, the influence of the temperature management on the geometric quality characteristics of the part was investigated. It was observed that a constant interlayer dwell time led to geometric irregularities in the part height and width. Monitoring the interlayer temperature is crucial in WAAM in order to maintain a constant temperature level along multiple layers for meeting the requirements for the geometry of the part and enabling near-net-shape manufacturing.