Baoyu Liu

The dynamic thermomechanical properties of wood–plastic composites (WPCs) are influenced by various factors, such as the selection of raw materials and processing parameters. To investigate the effects of different wood fiber content ratios and temperature on the loss modulus of WPCs, seven different proportions of Masson pine (Pinus massoniana Lamb.) and Chinese fir [Cunninghamia lanceolata (Lamb.) Hook.] mixed-fiber-reinforced HDPE composites were prepared using the extrusion molding method. Their dynamic thermomechanical properties were tested and analyzed. The storage modulus of WPCs showed a decreasing trend with increasing temperature. A reduction in the mass ratio of Masson pine wood fibers to Chinese fir wood fibers resulted in an increase in the storage modulus of WPCs. The highest storage modulus was achieved when the mass ratio of Masson pine wood fibers to Chinese fir wood fibers was 1:5. In addition, the loss modulus of the composites increased as the content of Masson pine fiber decreased, with the lowest loss modulus observed in HDPE composites reinforced with Masson pine wood fibers. The loss tangent for all seven types of WPCs increased with rising temperatures, with the maximum loss tangent observed in WPCs reinforced with Masson pine wood fibers and HDPE. A prediction method based on the Extreme Learning Machine (ELM) model was introduced to predict the dynamic thermomechanical properties of WPCs. The prediction accuracy of the ELM model was compared comprehensively with that of other models, including Support Vector Machines (SVMs), Random Forest (RF), Back Propagation (BP) neural networks, and Particle Swarm Optimization-BP (PSO-BP) neural network models. Among these, the ELM model showed superior data fitting and prediction accuracy, with an R² value of 0.992, Mean Absolute Error (MAE) of 1.363, and Root Mean Square Error (RMSE) of 3.311. Compared to the other models, the ELM model demonstrated the best performance. This study provides a solid basis and reference for future research on the dynamic thermomechanical properties of WPCs.

Improving the physical, mechanical, and creep properties of wood fiber-reinforced polymer composites is crucial for broadening their application prospect. In this research, seven types of high-density polyethylene (HDPE) composites reinforced with different mass ratios of Masson pine (Pinus massoniana Lamb.) and Chinese fir [Cunninghamia lanceolata (Lamb.) Hook.] were prepared by a two-step extrusion molding method. The mass ratios of the two fibers were 60:0, 50:10, 40:20, 30:30, 20:40, 10:50, and 0:60, respectively. The surface color, density, dimension stability, bending, tensile, impact properties, dynamic mechanical properties, and 24 h creep properties at a 10% stress level of the seven composites were investigated. Additionally, the Rule of Mixtures (ROM), the Inverse Rule of Mixtures (IROM), the Hirsch models, and the improved model were employed to simulate the mechanical properties, while the Findley index model, the two-parameter index model, and the modified ExpAssoc model were employed to simulate the creep performance of the composites. This study revealed that as the proportion of Chinese fir wood flour increased, the mechanical properties of the composites gradually improved, the storage modulus showed an increasing trend, while the loss modulus decreased, and the overall creep strain of the composites increased. Among the various models, the modified model simulated the mechanical properties of the composites the best, while the modified ExpAssoc model simulated the creep behavior most effectively.

The enhancement of the physical and mechanical properties and the anti-mildew performance of wood–plastic composites are of great significance for broadening their application field. In this research, bamboo fibers underwent treatments with safe, environmentally friendly bio-enzymes. Subsequently, a bamboo–plastic composite (BPC) was developed using the modified bamboo fibers and polyethylene. The effects of biological enzymatic treatments on the surface free energy, the chemical composition of the bamboo fibers, water resistance, thermal stability, bending performance, impact performance, and anti-mildew performance of the BPC samples were analyzed. This study revealed that treating bamboo powder with bio-enzymes (xylanase, lipase, laccase, pectinase, hemicellulase, or amylase) decreased the surface free energy and the polar components of the bamboo fibers while improving the surface O/C atomic ratio of the bamboo fibers. These enzyme treatments enhanced the water resistance, bending performance, and anti-mildew performance of the BPC samples. However, on the whole, the thermal stability of the composites decreased. Particularly, after hemicellulase treatment, the composites had the lowest water absorption, reflecting a decrease of 68.25% compared to the control group. With xylanase modification, the 24 h water absorption thickness swelling rate of the composites was the lowest, reflecting a decrease of 71.27% compared to the control group. After pectinase modification, the static bending strength and elastic modulus of the prepared composites were the highest, with an increase of 15.45% and 13.31%, respectively, compared to the unmodified group. After xylanase modification, the composites exhibited the best anti-mildew effect, with an anti-mold effectiveness of 74.67%. In conclusion, bio-enzyme treatments can enhance the physical and mechanical properties and anti-mildew performance of BPCs. This research provides a theoretical foundation for the preparation of high-performance wood–plastic composites.

In this study, the influence of fiber particle size on the mechanical properties of a wood-–plastic composite (WPC) was investigated using a combination of experimental measurements and numerical modeling. Four different sizes of wood fibers (10–20 mesh, 20–40 mesh, 40–80 mesh, and 80–120 mesh) were used to reinforce high-density polyethylene (HDPE), either separately or in combination. The different sizes of fibers produced varying properties in the resulting composites. The smallest fiber size (80–120 mesh) resulted in the lowest flexural and tensile properties, but the highest impact strength (15.79 kJ/m²) compared to the other three sizes (12.18–14.29 kJ/m²). Using a blend of fiber sizes resulted in improved mechanical properties. Composites containing a mix of 20–40 mesh and 40–80 mesh fibers exhibited the best flexural (strength 74.16 MPa, modulus 5.35 GPa) and tensile performance (strength 48.27 MPa, modulus 4.30 GPa), while composites containing a mix of all four fiber sizes had the highest impact-resistant strength (16.08 kJ/m²). Several models, including the Rule of Mixtures (ROM), the Inverse Rule of Mixtures (IROM), and the Hirsch models, were used to predict the performance of WPCs. The ROM model was found to be the most accurate in describing the mechanical properties of WPCs reinforced with multi-size wood fibers, based on the sum squared error (SSE) analysis.

Bamboo fibers are considered as a more attractive option for the reinforcement of wood plastic composites as compared to wood fiber due to its fast growth rate and good toughness. Heat treatment is an environment-friendly method of improving the integrated performance of bamboo materials. This paper highlights the heat treatment of bamboo fiber for suitable properties as reinforcements in bamboo plastic composites. The effects of vacuum heat treatment on the surface characteristics of bamboo fibers and the properties of bamboo plastic composites were analyzed by studying the chemical composition, surface elements and polarity of bamboo fiber before and after treatment, and the physical and mechanical properties of bamboo plastic composite. The results showed that after vacuum heat treatment, the bamboo fibers became darker and experienced a transition from green to red. Moreover, FTIR, XPS and contact angle analysis indicated that the hemicellulose content, the oxygen/carbon ratio and the polar component of the bamboo fiber had a decreasing trend as the treatment temperature increased. In addition, the 24 h water absorption and the 24 h thickness expansion rate of the water absorption showed a trend of first decreasing and then increasing as the treatment temperature increased, while the bending performance of bamboo plastic composite showed a trend of increasing first and then decreasing as a result of increased treatment temperature. Therefore, a combined process of vacuum heat treatment and the addition of MAPE could improve the physical and mechanical properties of bamboo plastic composites to a certain extent.