Changhao Shan

As an indispensable material in construction and engineering, concrete’s mechanical properties and permeability are crucial for structures’ stability and durability. In order to reasonably assess and improve the durability of fracture-containing concrete structures and to enhance the sustainable working life of concrete structures, this research investigated the seepage characteristics of fracture-containing concrete and its mechanical property deterioration under fracture–seepage coupling by testing the permeability and strength of concrete samples before and after water penetration using triaxial seepage test and mechanical strength test. The results show that the fracture–seepage coupling action significantly affects the permeability characteristics and mechanical strength of fracture-containing concrete. In particular, the strength of concrete samples containing a single fracture decreased with increased fracture angle, with a maximum decrease of 32.8%. The fracture–seepage–stress coupling significantly reduced the strength of the fracture-containing concrete samples, which was about twice as much as the strength of the no-fracture concrete samples. Different fracture angles affect the mode of fracture expansion and damage (The fracture angle varies from small to large, and the damage form of concrete changes from tensile damage to tensile–shear composite damage). Moreover, the coupling effect of fracture–seepage–stress will further increase fracture-containing concrete’s fragmentation in the damage process. Therefore, improving the seepage and fracture resistance of concrete plays a vital role in improving the sustainable working life of concrete structures.

For underground coal mining techniques such as gob-side entry retaining (GER) or gob-side entry driving (GED), the stability of yield pillars is paramount. A well-designed yield pillar aims to withstand mining-induced stresses. This study delves into the impact of bi-terminal cable support on the stability of such pillars. Utilizing 30 distinct numerical models, each with varying pillar width/height (w/h) ratios and diverse cable support methodologies, our findings suggest an upward trend in both peak and residual strength in response to heightened support strength. Notably, pillars with a wider configuration exhibited a more pronounced increase in peak strength compared to their narrower counterparts, while the latter showcased a more pronounced residual strength enhancement. Additionally, the residual/peak strength ratio was smaller in narrower pillars and increased with the increase in the cable support strength. In view of the surrounding rock mass’s support stress distribution, numerical modelling was adopted to analyze the underlying support mechanism. The results showed the support stress zones extended farther on both sides of pillars with the decrease in the row spacing, which made the radial stresses rise effectively and ameliorated the coal pillar’s stress state. Finally, with the 8311 operation advancing towards the station, the deformation amplitude of the coal pillar was only 2.28%, and the stability of the coal pillar was effectively maintained.

For underground water reservoirs in coal mines, the complex water-rich environment and changing overburden stress can damage coal pillar dams. In this paper, the coal samples from coal seam 2² of Shangwan coal mine were taken as research objects and the damage mechanism and characteristics of coal samples with different moisture content and wetting-drying cycles under cyclic loading were investigated. The results show that as the moisture content and wetting-drying cycles increase, the post-peak stage of the coal samples under cyclic stress becomes obvious, and the hysteresis loop changes from dense to sparse. Compared to the uniaxial compression experiment, when w = 5.28% (the critical water content), mechanical parameters such as peak strength and modulus of elasticity decrease the most. Under cyclic loading, the damage mode of both sets of coal samples was tensile damage, but the increase in wetting-drying cycles promotes the development of shear fractures. For evaluating fracture types, the RA-AF density map is more applicable to wetting-drying cycle coal samples, whereas for the coal samples with different moisture contents this should be carried out with caution. This study can provide some theoretical basis for the stability evaluation of coal pillar dams in underground water reservoirs.