Meysam Keshavarz

In recent, the efforts to reduce environmental pollution by developing biodegradable material has received wide interest. The aim of this paper is to investigate the effect of durian skin fiber (DSF) on the properties of thermoplastic cassava starch (TPCS) matrix as the biodegradable material. The composites were prepared by using hot press technique to convert the starch into thermoplastic starch polymer. The effects of incorporating different amount of DSF (0-50 wt.%) on the matrix was evaluated using several testings, i.e., water absorptions, water solubility, thickness swelling, moisture content, biodegradation analysis and density measurement. The results show that incorporation of DSF has reduce the water absorption characteristic of the material. Thickness swelling of the sample were increase following the addition of DSF into the TPCS matrix, indicating improve environmentally friendly properties. Water solubility of the composites showed a decreasing trend with increasing DSF content. The morphology of the samples shows adhesion of fiber and matrix which indicates good compatibility between this component. Meanwhile, there is no apparent changes on the density of the composites following the incorporation of fiber. Overall, this finding shows that DSF has potential to improve the functional characteristics of TPCS matrix as alternative green material.

The aim of this paper is to investigate the effect of cogon grass fiber (CGF) on the thermal and mechanical properties of thermoplastic cassava starch (TPCS)/beeswax matrix. The alteration of TPCS/beeswax reinforced with cogon grass fiber was performed by incorporating various amount of CGF (0,10,20,30,40 wt.%) into the polymer matrix. The samples were then evaluated using thermogravimetric analysis and tensile test. The findings showed that the thermal properties of the composite were slightly improved as the CGF content increase. The mechanical test showed that the tensile strength and tensile modulus increased with the addition of the CGF. However, the elongation at break showed a decreased pattern following the increasing content of CGF compared to the 0% of fiber content. In general, the findings from this study have shown that the TPCS/beeswax reinforced with the CGF composite has improved the functional properties of the composites compared to the TPCS matrix.