Dejin Qiu

The current study focuses on developing a novel 3D mathematical model to simulate the hematite pellet reduction process by integrating a three-step random pore model with a computational fluid dynamic framework, taking into account the mass and heat transfer in a hydrogen (H ₂ ) atmosphere. The model incorporates critical factors such as porosity variation and gas evolution to capture their interactions and influence on reduction behaviour across different temperatures. Reduction experiments use a spherical pellet that is reconstructed from CT images based on X-ray microcomputed tomography to represent the real internal pellet structure. The results show that the model can predict the porosity variation and gas diffusion during the reduction process precisely. The complete conversion time decreases from 3300 s at 973 K to 800 s at 1273 K. The water vapour and hydrogen gas species are more uniformly distributed throughout the pellet and more advanced at 1273 K than at 973 K. Additionally, the accumulation of water vapour within the pores forms a diffusion barrier, restricting hydrogen from reaching the reaction sites. The accuracy and reliability of the developed model were validated through comparison with our previously conducted experimental data. This model provides a robust framework for the realistic, dynamic modelling of industrial reduction processes.

Electric arc furnace dust (EAFD) is a zinc-containing solid waste generated during steelmaking, and advanced recycling strategies are needed to facilitate the recovery of valuable zinc. This study investigated the microwave-assisted carbothermic reduction in EAFD using coke as a reductant, with a focus on temperature (900–1100 °C), holding time (0–60 min), and the C/Zn molar ratio (3–5). The results demonstrated that the zinc removal rate exhibited positive correlations with both temperature and time. Under optimized conditions (1100 °C, 60 min), a zinc removal rate of 95.45% was achieved, accompanied by a complete decomposition of the ZnO phases. Furthermore, increasing the C/Zn molar ratio enhanced the zinc recovery efficiency and product purity. Isothermal kinetic analyses indicated that the reaction proceeds in two stages: during the initial stage (0–30 min), the process was governed by three-dimensional diffusion control with an activation energy of 146.50 kJ/mol, while the final stage (30–60 min) transitioned to chemical reaction control with an activation energy of 267.32 kJ/mol. Comparative assessments indicated that microwave processing significantly reduced the activation energy compared to conventional heating methods. These findings suggest that microwave-assisted reduction is capable of attaining a high-grade recovery of Zn from EAFD, thus opening up new avenues for the resource-oriented utilization of EAFD.

Electric arc furnace dust (EAFD) is a hazardous by-product of steel production. As global steel output increases, substantial amounts of EAFD are produced, which causes significant environmental issues. EAFD contains quantities of Fe and Zn, which could be reused as raw materials in the steelmaking process. However, zinc oxides can be reduced and vaporized during this process, forming zinc vapor that contaminates equipment surfaces and causes damage. Consequently, various pyrometallurgical methods have been proposed for zinc removal from EAFD. Due to the extensive usage of carbonaceous materials, these methods contribute to significant CO₂, raising concerns about greenhouse gas emissions. Microwave heating offers an efficient, energy-saving, and environmentally friendly alternative to pyrometallurgical approaches. EAFD can generate heat under microwave irradiation without carbon addition, which means the CO₂ emissions can be reduced by replacing the reductant in the microwave heating process. Furthermore, microwaves enhance zinc removal reactions to a certain extent, resulting in higher efficiency. Thus, employing microwave heating for EAFD processing has significant potential for future development. This paper reviews recent research on using microwave heating for zinc removal from EAFD, focusing on the heating behavior of EAFD in microwaves and the mechanisms of zinc removal. This review will be crucial for researchers working on processing EAFD using microwave heating and could help guide the development of more sustainable and efficient methods.

Electric arc furnace dust (EAFD) is a hazardous by-product of steel production. As global steel output increases, substantial amounts of EAFD are produced, which causes significant environmental issues. EAFD contains amounts of Fe and Zn, which could be reused as raw materials in the steelmaking process. However, zinc oxides can be reduced and vaporized during this process, forming zinc vapor that contaminates equipment surfaces and causes damage. Consequently, various pyrometallurgical methods have been proposed for zinc removal from EAFD. Due to the extensive usage of carbonaceous materials, these methods contribute to significant CO2, raising concerns about greenhouse gas emissions. Microwave heating offers an efficient, energy-saving, and environmentally friendly alternative to pyrometallurgical approaches. EAFD can generate heat under microwave irradiation without carbon addition, which means the CO2 emissions can be reduced by replacing the reductant in the microwave heating process. Furthermore, microwaves enhance zinc removal reactions to a certain extent, resulting in higher efficiency. Thus, employing microwave heating for EAFD processing has significant potential for future development. This paper reviews recent research on using microwave heating for zinc removal from EAFD, focusing on the heating behavior of EAFD in microwaves and the mechanisms of zinc removal. This review will be crucial for researchers working on processing EAFD using microwave heating and could help guide the development of more sustainable and efficient methods.

Ultrahigh-speed continuous casting is a critical element in achieving high-efficiency continuous casting. In the present work, a three-dimensional model of a 160 mm × 160 mm billet ultrahigh-speed continuous casting mold was developed for use in studying the influences of different casting parameters on molten steel flow. The results showed that the flow pattern in the mold was not associated with its casting speeds, submerged entry nozzle (SEN) immersion depths, or inner diameters. Variation in casting speeds significantly affected the liquid level of the steel–slag interface. Its liquid level fluctuation was reasonable at an SEN immersion depth of 80 mm. Its impact depth reached the shallowest point, which was conducive to upward movement within high-velocity and high-temperature regions, and accelerated the floating of non-metallic inclusions. Expanding the inner diameter of the SEN could effectively weaken the initial kinetic energy of the jet. However, it may cause a deeper impact depth and a degree of upward movement in the raceway, which exhibited the shallowest impact depth in the jet and the most reasonable behavior of molten steel at a liquid level for which the inner diameter of the SEN was 40 mm.

Silicon nitride (Si₃N₄) and silicon powder (Si) are two kinds of harmful solid waste in industrial production. As an environmental and low-consumption method, the cold-bonding technique is a novel method to utilize the problem of powder resource cycling. In this experiment, mechanical and high-temperature properties of Si and Si₃N₄ briquettes were studied after cold bonding. The results are as follows: (1) The compressive strength of the Si and Si₃N₄ briquettes increased with the improvement of molding pressure. With the same binder (1 wt.%) and water (10 wt.%) addition, the compressive strength of the Si₃N₄ briquette arrived at 12,023.53 N under 40 Mpa molding pressure, which is much higher than that of the Si briquette (942.40 N). The Si particles are uneven and irregular, which leads to an intense arch bridge effect in the Si briquette and the compressive strength decrease. Compared with Si powder, the particle size and shape of Si₃N₄ is small, uniform, and regular. The influence of the arch bridge effect is smaller than that in the Si briquette. (2) After being treated at 1473 K for 1 h, the compressive strength of the Si briquette increased to 5049.83 N, and the compressive strength of the Si₃N₄ briquette had a slight change. The surface of the briquettes was contacted with oxygen and reacted to form an outer shell which mainly contains SiO₂ in the high-temperature treatment. FT-IR results have shown there were no extra impurities in cold-bonded briquettes when using the organic binder. (3) The microstructure of the cross section of the Si and Si₃N₄ briquettes after high-temperature treatment presented that oxygen entered the briquette through the pores and continued to react with the Si and Si₃N₄. The outer shell of the Si briquette grew and thickened continuously with the oxygen spreading in the Si briquette. However, because of the smaller particle size and regular shape, little oxygen diffused in the Si₃N₄ briquette. The outer shell of the Si₃N₄ briquette is fairly thin, so the compressive strength did not change too much.