Both commercial and research applications of wire arc additive manufacturing (WAAM) have seen considerable growth in the additive manufacturing of metallic components. However, there remains a clear lack of a unified paradigm for toolpath generation when slicing parts for WAAM deposition. Existing toolpath generation options typically lack the appropriate features to account for all complexities of the WAAM process. This manuscript explores the key slicing challenges specific to toolpaths for WAAM geometry and pairs each consideration with multiple solutions to mitigate most negative effects on completed components. These challenges must be addressed to minimize voids, prevent bead collapse, and ensure deposited components accurately approximate the desired geometry. Slicing considerations are grouped into four general categories: geometric, process, thermal, and productivity. Geometric considerations are addressed with overhang compensation, corner-sharpening, and toolpath-smoothing features. Process considerations are addressed with start point configuration and controls for the bead lengths and end points. Thermal and productivity considerations are addressed with island optimization, multi-material printing, and connected insets. Finally, tools for the post-processing of generated G-code are explored. Overall, these solutions represent a critical set of slicing features used to improve generated toolpaths and the quality of the components deposited with those toolpaths.

The U.S. Department of Energy's Office of Scientific and Technical Information

The U.S. Department of Energy's Office of Scientific and Technical Information

Metal Big Area Additive Manufacturing (MBAAM) is a novel wire-arc additive manufacturing method that uses a correction-based approach developed at the Oak Ridge National Laboratory (ORNL). This approach is an integrated software method that minimizes the dynamic nature of welding and compensates for build height. The MBAAM process is used to fabricate simple geometry thin walled specimens, using a C-Mn steel weld wire, to investigate the scatter in mechanical properties and correlate them to the underlying microstructure. The uni-axial tensile tests show isotropic tensile and yield properties with respect to building directions, although some scatter in elongation is observed. Large scatter is observed in the Charpy Impact tests. The microstructure characterization reveals mostly homogenous ferrite grains with some pearlite, except for some changes in morphology and grain size at the interface between the build and the base plate. The measured properties and microstructure are compared with the toughness and strength values reported in the literature, and a hypothesis is developed to rationalize the differences. Overall, the MBAAM process creates stable, isotropic, and weld-like mechanical properties in the deposit, while achieving a precise geometry obtained through a real-time feedback sensing, closed loop control system.