Zhanglin Sun

Bird pest control has become a major task for the operation and maintenance of distribution network lines. Epoxy resin that cures quickly at room temperature can be used to coat locations where birds frequently build their nests. However, epoxy resin has enormous internal stress and is brittle, so it is essential to toughen it. In this paper, for a room temperature curing system composed of polyurethane-modified epoxy resin and a polythiol curing agent, three kinds of particles, i.e., Al₂O₃, SiO₂, and Mg(OH)₂, were used to modify a polyurethane modified epoxy resin. Orthogonal experiments were designed to study the effects of different fillers on the comprehensive properties of polyurethane-modified epoxy resins. The experimental results showed that there were not only independent effects of different kinds if particles on the resin, but also synergistic effects of multiple particles. Nanoparticles can reduce the defects introduced by microparticles to a certain extent and improve the mechanical and electrical properties of the resin. The overall performance of the resin was optimized when the amounts of SiO₂, Al₂O₃, and Mg(OH)₂ were 1.7%, 2.5%, and 7%, respectively. The tensile strength of the resin was increased by 70%, the elongation at a break by 67.53%, and the breakdown strength by 20.31% compared with before the addition of filler. The microscopic morphology and thermal properties of the resin before and after the addition of filler were also studied. Adding fillers caused more cracks to absorb part of the energy when the resin matrix was stressed and increased the rigidity of the resin matrix and the resin’s glass transition temperature (T_g) by 13.48 °C. Still, the temperature corresponding to the maximum rate of weight loss (T_max) remained unchanged.

Epoxy resin insulation materials are mainly derived from petrochemical materials which have the disadvantages of resource consumption and environmental pollution. In order to cure bisphenol A epoxy resin, a maleopimaric anhydride (MPA) curing agent was prepared from rosin, a renewable resource, and blended with a petroleum-based curing agent (methylhexahy-drophthalic anhydride). The influence of maleopimaric anhydride content on the initiation and growth characteristics of electrical trees was studied and analyzed in this paper using molecular dynamics simulation (MD) and electrical tree tests at an 18-kilovolt power frequency voltage. When the MPA content used was ≤10%, the free volume percentage of the curing system increased with MPA content, and thus the initiation voltage became lower; when the MPA content was ≥20%, the hydrogenated phenanthrene ring structure content increased significantly with increasing MPA content, and the rigidity of the curing system increased significantly; thus, the initiation voltage gradually increased. MPA4 had an 11.11% higher initiation voltage than the petroleum-based control group. The effect of the polar rigid structure within the curing system significantly inhibited the growth rate and length of electrical trees as MPA content increased. Electrical trees developed into light-colored, thin, and narrow dendritic structures when the MPA content reached 40%. The results show that curing epoxy resin with the rosin-based curing agent maleopimaric anhydride (MPA), in place of a petroleum-based curing agent, can produce environmentally friendly resins with excellent electrical tree resistance and potential application prospects.