Molding in thermoplastic polymers using ultrasonic hot embossing technology is promising due to its high precision reproducibility. To understand, analyze and apply the formation of polymer microstructures by the ultrasonic hot embossing method, it is necessary to understand dynamic loading conditions. The Standard Linear Solid model (SLS) is a method that allows analyzing the viscoelastic properties of materials by representing them as a combination of springs and dashpots. However, this model is general, and it is challenging to represent a viscoelastic material with multiple relaxations. Therefore, this article aims to use the data obtained from dynamic mechanical analysis for extrapolation in a wide range of cyclic deformations and to use the obtained data in microstructure formation simulations. The formation was replicated using a novel magnetostrictor design that sets a specific temperature and vibration frequency. The changes were analyzed on a diffractometer. After the diffraction efficiency measurement, it was found that the highest quality structures were formed at a temperature of 68 °C, a frequency of 10 kHz, a frequency amplitude of 1.5 µm and a force of 1 kN force. Moreover, the structures could be molded on any thickness of plastic.

Polymeric microstructures and microchannels are widely used in biomedical devices, optics, microfluidics and fiber optics. The quality, the shape, the spacing and the curvature of microstructure gratings are influenced by different mechanisms and fabrication techniques used. This paper demonstrates a cost-effective way for patterning high-aspect-ratio thermoplastic microstructures using thermal imprint technology and finite element modeling. Polymeric materials polypropylene (PP), polyethylene terephthalate glycol (PETG), polyvinyl chloride (PVC) and styrene-acrylonitrile (SAN) were chosen for the experimental investigations. A finite element model was constructed to define the most suitable parameters (time, heating temperature, pressure, etc.) for the formation of microstructures using the thermal imprint procedure. To confirm the relevance of the finite element model, different types of PP, PETG, PVC and SAN microstructures were fabricated using theoretically defined parameters. Experimental investigations of imprinted microstructures’ morphological and optical properties were performed using scanning electron microscopy, atomic force microscopy and a diffractometer. Obtained results confirmed the relevance of the created finite element model which was applied in the formation of high-aspect-ratio microstructures. Application of this model in thermal imprint would not only reduce the fabrication time, but also would highly increase the surface quality and optical properties of the formed structures.