Carlos Galarce

Structural lumber is designed to meet the technical standards that ensure safety, cost-effectiveness, and sustainability. However, some tree species face limitations in their growth, which restricts their widespread use. An example of this is Nothofagus alpina, which has excellent mechanical properties but is not utilized much due to the challenges in extracting its timber and poor utilization, mainly because of the length of the wood. There is little information concerned with the uses and better management of small pieces using Nothofagus species, but it is still insufficient. This study investigates the adhesion performance of green-glued finger joints with varying wood ring orientations and moisture contents ranging from 21% to 25% using Nothofagus alpina. The primary aim is to assess how ring orientation and wet timber affect the green gluing process for creating larger wood pieces than sawn wood. The resulting products could meet the standards for wood serviceability number three for native Chilean wood. The findings indicate that finger joint performance improves with higher timber moisture levels. However, the orientation of the wood fibers did not significantly affect the performance under the tested conditions. It is important to note that this effect may become more significant near the fiber saturation point. These findings emphasize the need for a detailed protocol on the green gluing technique for Nothofagus alpina and the associated drying and surface processes in finger joint construction.

Appraising and protecting forests requires a management plan and the creation of innovative products for the market. The development of the green gluing technique could add value to native timber. However, there is a lack of knowledge concerning the response and the productive process of Nothofagus species using this technique. This work investigated the viability of implementing the green gluing method using three types of Nothofagus. Wood pieces were made using a one-component polyurethane adhesive. Delamination, shear tests, morphological characterization, and bond line thickness analysis tested their capacity. The results showed a variable response depending on the Nothofagus type, where the surface treatment could improve the green gluing performance. The findings highlight the relevance of increasing knowledge about the essayed species and their preparation to maintain their natural moisture condition.

Wood is a sustainable and renewable material with a lower carbon footprint than other materials. However, its transformation into engineered products industrially, such as glulam, requires kiln drying, which implies energy consumption and loss of wood resources. Recent research has carried out green gluing, a variant of glulam characterized by a reduction of the drying process. Interest in it has increased as a new method of improving the use of wood that does not meet industry standards. It has been accomplished by developing adhesives for wood with high moisture content, but the variables involved are not yet completely understood. Therefore, conducting further research and analyzing the relevant publications is necessary. Bibliometric analysis was the method used, which included documents stored (from 2000 to 2020) in Scopus (Elsevier), Web of Science (Clarivate Analytics), and SciELO Citation Index (Web of Science—Clarivate Analytics) databases. The bibliometric analysis identified three main areas to develop: glue wood, glue properties, and analysis methods. The studies were concentrated on a few countries and research groups. The main progress has been made in synthetic and natural (or environmentally friendly) glue topics. The improvement of technique could enlarge the opportunities for collaboration and innovation in wood material science.

Deficient disinfection systems enable bacteria to form in drinking water; these can invade plumbing systems even if the pipes are composed of antibacterial materials such as copper. Severe copper corrosion by microorganisms and their subsequent release into the water system are evidenced by the blue water phenomenon. Proper monitoring and control can reduce such undesirable effects on water quality. However, a lack of data from analysis under actual conditions has limited the development of useful predictive tools and preventive strategies. In this work, an experimental aging system was connected to a drinking water network affected by the blue water phenomenon. The microbially influenced corrosion (MIC) was evaluated by studying the dynamics of the formed bacterial community and its relationship with copper corrosion and the release of copper. The results suggest that the conformation and composition of the biofilm attached to the surface influence the measured parameters. The corrosion rate was variable throughout the sampling time, with the highest value recorded after one year of aging. The composition of biofilms also changed with time; however, the genus Pseudomonas was ubiquitous over the sampling time. No relationship between the corrosion rate and the biofilm age was observed, thereby suggesting that MIC is a dynamic phenomenon that requires further study.

The effects of tidal cycles associated with the water level on the biocorrosion of stainless steel AISI 316L were studied. Steel coupons were exposed to different conditions of immersion in mesocosms fed by fresh seawater either continuously or in accordance with the periodicity of natural tides. After 5 and 15 weeks, all coupons were found to have undergone ennoblement associated with the formation of a biofilm. Analysis of the composition of the bacterial community using denaturing gradient gel electrophoresis (DGGE) revealed differences in the biological succession. After 15 weeks, exposure to the simulated tidal conditions resulted in biofilms with lesser bacterial richness; the corresponding rate of corrosion, as determined by weight loss, was about 40 times lower compared to the case for the continuous exposure to seawater. Phylogenetic analysis of selected DGGE bands and the inspection of biofilm morphologies revealed that the faster rate of corrosion was associated with the presence of iron-oxidizing Zetaproteobacteria and eukaryotic photosynthetic microorganisms. On the other hand, intermittent exposure to seawater resulted in the succession of microorganisms resistant to the stress associated with sudden environmental changes, which was associated with a low rate of corrosion.