Nano-crystalline diamond has been extensively researched and applied in the fields of tribology, optics, quantum information and biomedicine. In virtue of its hardness, the highest in natural materials, diamond outperforms the other materials in terms of wear resistance. Compared to traditional single-crystalline and poly-crystalline diamonds, nano-crystalline diamond consists of disordered grains and thus possesses good toughness and self-sharpening. These merits render nano-crystalline diamonds to have great potential in tribology. Moreover, the re-nucleation of nano-crystalline diamond during preparation is beneficial to decreasing surface roughness due to its ultrafine grain size. Nano-crystalline diamond coatings can have a friction coefficient as low as single-crystal diamonds. This article briefly introduces the approaches to preparing nano-crystalline diamond materials and summarizes their applications in the field of tribology. Firstly, nano-crystalline diamond powders can be used as additives in both oil- and water-based lubricants to significantly enhance their anti-wear property. Nano-crystalline diamond coatings can also act as self-lubricating films when they are deposited on different substrates, exhibiting excellent performance in friction reduction and wear resistance. In addition, the research works related to the tribological applications of nano-crystalline diamond composites have also been reviewed in this paper.

Diamond films prepared by chemical vapor deposition will exhibit different surface morphologies, which are determined by the texture and the structural perfection of the deposited diamond. In general, its surface morphology can be controlled by adjusting the deposition conditions. In the present work, textured diamond film was deposited on single crystalline silicon through pre-seeding by diamond nanosheets, rather than controlling the deposition conditions. The employed diamond nano-sheets were prepared by cleavage along a plane, exhibiting good crystallinity. Before chemical vapor deposition, the as-prepared diamond nano-sheets were pre-seeded on the surface of single crystalline silicon as nucleation sites for diamond growth. SEM and XRD results show that the prepared diamond films have a texture. FIB observation reveals that diamonds homogeneously grow on the pre-seeded diamond nano-sheets during chemical vapor deposition, achieving the diamond film with texture. Our work provides a new strategy to prepare textured diamond film.