Xincai Li

Grasses are potential candidate to replace wood as a raw material for pulping and paper making, and several processes have been developed to produce grass pulp. In this study, wheat straw was used as raw material, and the possibility of sequential treatment with a mechanical method and deep eutectic solvent (DES) to prepare high-quality dissolving pulp was explored. Firstly, the wheat straw was mechanically treated, and then the wheat straw was delignified using a choline chloride–lactic acid deep eutectic solvent. The results showed that the optimal treatment conditions of deep eutectic solvent were 110 °C, 6 h, and a solid–liquid ratio (ratio of pulp to DES) of 1:40. The removal rate of lignin was 82.92%, the glucose content of pulp was increased by 11.42%. The DES recovery rate was further calculated, and the results showed that the DES recovery rate was more than 50% with rotary evaporation. The pulp viscosity after bleaching was 472 mL/g, and the α-cellulose accounted for 81.79%. This treatment has advantages in biomass refining, and the total utilization rate of wheat straw reaches 72%. This study confirmed that combined mechanical and deep eutectic solvent treatment can effectively remove lignin from wheat straw to produce high-quality wheat straw dissolving pulp.

Hydrogels have attracted much attraction for promising flexible electronics due to the versatile tunability of the properties. However, there is still a big obstacle to balance between the multi-properties and performance of wearable electronics. Herein, we propose a salt-percolated nanocellulose composite hydrogel which was fabricated via radical polymerization with acrylic acid as polymer networks (NaCl-CNCs-PAA). CNCs were utilized as a reinforcing agent to enhance the mechanical properties of the hydrogel. Moreover, the abundant hydroxyl groups endow the hydrogel with noncovalent interactions, such as hydrogen bonding, and the robustness of the hydrogel was thus improved. NaCl incorporation induced the electrostatic interaction between CNCs and PAA polymer blocks, thus facilitating the improvement of the stretchability of the hydrogel. The as-obtained hydrogel exhibited excellent stretchability, ionic conductivity, mechanical robustness and anti-freezing properties, making it suitable for self-powered sensing applications. A single-mode triboelectric nanogenerator (C-TENG) was fabricated by utilizing the composite hydrogel as electrodes. This C-TENG could effectively convert biomechanical energy to electricity (89.2 V, 1.8 µA, 32.1 nC, and the max power density of 60.8 mW m⁻² at 1.5 Hz.) Moreover, the composite hydrogel was applied for strain sensing to detect human motions. The nanocellulose composite hydrogel can achieve the application as a power supply in integrated sensing systems and as a strain sensor for human motion detection.

The application of silver nanoparticles (AgNPs) in antibacterial materials, glucose detection, etc., is of broad interest for researchers around the world. Nanocellulose with many excellent properties can be used as a carrier and stabilizer to assist in the synthesis of AgNPs. In this study, cellulose nanofibrils (CNFs) and cellulose nanocrystals (CNCs) were used to assist in the synthesis of AgNPs under the reduction of glucose and detection of glucose concentration under different conditions. Transmission electron microscopy (TEM) analysis showed that the AgNPs in the nanocellulose-AgNPs (NC-AgNPs) system were roughly spherical and randomly distributed on the nanocellulose. In the whole reaction system, when the concentration of nanocellulose is 0.11 mg/mL, the concentration of silver ammonia solution is 0.6 mM, and the mixing time is 2.5 h, according to the UV-Vis analysis, the absorbance of CNF-AgNPs at 425 nm exhibited a good linear relationship (R² = 0.9945) with the glucose concentration range (5–50 μM), while the absorbance of CNC-AgNPs at 420 nm showed a good linear relationship (R² = 0.9956) with the glucose concentration range (5–35 μM). The synthesis of NC-AgNPs can be further developed into a sensor with higher sensitivity and higher stability for detecting glucose concentration and a material with antibacterial effects.