Damla Güneş Ünlü

Purpose: This in vitro study aimed to evaluate the effects of post material and cement type on the pull-out force of prefabricated glass-fiber, PEEK, and PEKK posts. Methods: Sixty extracted human mandibular premolars were prepared with standardized root canals and allocated into six groups (n = 10) according to post material (glass-fiber, PEEK, PEKK) and luting cement (resin or glass ionomer). PEEK and PEKK posts were CAD-CAM fabricated from prefabricated discs. All specimens underwent thermocycling (6000 cycles, 5–55 °C) prior to pull-out force testing on a universal testing machine, and failure modes were classified as adhesive, cohesive, or mixed. Because variance homogeneity was not satisfied, pull-out force values were logarithmically transformed (Log10) before two-way ANOVA and Bonferroni-adjusted post hoc analyses. Results: Post material (p = 0.026), cement type (p < 0.001), and their interaction (p = 0.012) significantly influenced pull-out force. Under resin cement, no statistically significant differences were detected among glass-fiber, PEEK, and PEKK posts. Under glass ionomer cement, PEEK and PEKK posts demonstrated significantly higher pull-out force than glass-fiber posts. The highest mean pull-out force was observed for glass-fiber posts luted with resin cement. The effect of post material on pull-out force was dependent on the luting cement. PEEK posts luted with resin cement showed no significant difference in pull-out force compared with conventional glass-fiber posts, supporting their potential as an alternative post material. Further studies are needed to evaluate the clinical performance of PEEK posts.

Aim: The aim of this study is to evaluate the effects of Er,Cr:YSGG laser debonding on the mechanical properties of aged and non-aged lithium disilicate ceramics. Material and Methods: A total of 36 lithium disilicate samples with dimensions of 14x4x1 mm were prepared. Half of the samples underwent 5000 thermal cycles to simulate artificial aging. The aged and non-aged samples were divided into two subgroups: one subgroup was designated as the control group and did not receive laser treatment, while the other subgroup was treated with Er,Cr:YSGG laser for debonding (n=9). The flexural strength and modulus of the lithium disilicate samples were assessed using three-point bending tests before and after artificial aging. The surface roughness of a sample that did not undergo the three-point bending test was measured with AFM, its microhardness was assessed using Vickers hardness tests, and surface morphology was examined with FESEM. Two-way ANOVA and Bonferroni correction to determine the significance of the results were used for statistical analysis. Results: The results indicated that aging significantly reduced the flexural strength (p=0.031), however, laser debonding did not have a significant effect on the flexural strength or modulus of either aged or non-aged samples. Conclusion: Laser debonding effectively removes lithium disilicate restorations without compromising their mechanical properties, supporting their reuse in clinical practice. It is important to note that aging reduces the flexural strength of lithium disilicate ceramics.

This study was purposed to assess the impact of ageing and resin cements polymerized with different modes on the removal time of lithium disilicate (LiSi) ceramics using Er,Cr:YSGG laser. Ninety LiSi slabs (6 × 6 × 1 mm) were cemented to freshly extracted bovine teeth using cements polymerized with different modes (light-curing (LC), dual-curing (DC), self-curing (SC)). The specimens were divided into subgroups according to ageing conditions (no thermal cycling, 5000 or 30,000 thermal cycling). After that, Er,Cr:YSGG laser was applied until LiSi slabs were debonded; the removal time was recorded. Vickers microhardness test, SEM and EDS analyses were performed for specimens with the longest exposure time to laser application in the groups. One uncemented sample was also used as a control. Data were analyzed with two-way ANOVA and Tukey post hoc test. Ageing and cement polymerization mode significantly affected the removal time of LiSi specimens. The removal time for the self-curing resin cement group (22.67 ± 12.68 s) was significantly longer than for cements polymerized with other methods (LC = 10.833 ± 7.28 s, DC = 12.0 ± 7.96 s). Removal time was significantly reduced after ageing in all polymerization modes; however, there were no significant differences between 5000 (11.83 ± 7.52 s) and 30,000 (11.83 ± 7.26 s) thermal cycling groups. Self-curing resin cements had prolonged the laser-aided removal time for LiSi ceramics. It can be concluded that Er,Cr:YSGG laser-aided removal of LiSi veneers after clinical use can be done more faster than its immediate removal.

AMAÇ: Bu çalışmanın amacı, farklı geçici yapım teknikleri ile kullanılan geçici materyallerinin renk stabilitelerine polisaj patlarının etkisinin araştırılmasıdır. GEREÇ YÖNTEMLER: Üç farklı yöntemle kullanılan geçici materyalinden 90 adet 18x15x2 mm boyutlarında örnekler hazırlanmıştır. Polimetil metakrilat (PMMA) ve bis- akrilik kompozit rezin örnekler teflon kalıp yardımı ile, CAD/CAM PMMA örnekler hassas kesme cihazı yardımı ile hazırlanmıştır. Örneklerin şekillendirilmesinin ardından fazlalıklar canavar frez ile kaldırılmış ve tüm örnekler 600 grid su zımparası ile zımparalanmıştır. Daha sonra her materyalden örnekler 3 gruba (n=10) ayrılmıştır. Birinci gruptaki örneklere yüzey işlemi uygulanmamıştır. İkinci gruptaki örneklere universal polisaj patı ve üçüncü gruptaki örneklere elmas içerikli pat uygulanmıştır. Distile suda 24 saat bekletmenin ardında örneklerin başlangıç L, a, b değerleri ölçülmüştür. 6 gün kahve solüsyonunda bekletilmiş ve tekrar renk değerleri ölçülerek ∆E (renk değişimi) değeri hesaplanmıştır. Elde edilen veriler iki yönlü ANOVA ile değerlendirilmiş, gruplar arası farkların tespiti için Tukey’s HSD post hoc testi yapılmıştır (p<0.05). BULGULAR: Faklı yöntemle kullanılan geçici materyallerinin ∆E değeri istatistiksel olarak anlamlı bulunmuştur. PMMA toz likit karıştırmalı üründe en düşük ∆E değeri bulunurken en yüksek ∆E değeri bis- akrilik kompozit rezinde bulunmuştur. Ancak farklı polisaj patlarının ∆E değerine etkisi olmadığı tespit edilmiştir. SONUÇ: Uzun dönem kullanılması planlanan sabit geçicilerde, renk stabilitesine, materyal seçimi uygulanacak yüzey işleminden daha fazla etki etmektedir.

Akademisyen Yayınevi yöneticileri, yaklaşık 30 yıllık yayın tecrübesini, kendi tüzel kişiliklerine aktararak uzun zamandan beri, ticarî faaliyetlerini sürdürmektedir. Anılan süre içinde, başta sağlık ve sosyal bilimler, kültürel ve sanatsal konular dahil 1000 kitabı yayımlamanın gururu içindedir. Uluslararası yayınevi olmanın alt yapısını tamamlayan Akademisyen, Türkçe ve yabancı dillerde yayın yapmanın yanında, küresel bir marka yaratmanın peşindedir. Bilimsel ve düşünsel çalışmaların kalıcı belgeleri sayılan kitaplar, bilgi kayıt ortamı olarak yüzlerce yılın tanıklarıdır. Matbaanın icadıyla varoluşunu sağlam temellere oturtan kitabın geleceği, her ne kadar yeni buluşların yörüngesine taşınmış olsa da, daha uzun süre hayatımızda yer edineceği muhakkaktır. Gülüş Tasarımında Estetik Kriterler Merve ÜNAL Aysıla ŞİMSEK TEKELİ Gamze PAKEN Bengisu YILDIRIM Diş Hekimliğinde Güncel Estetik Materyaller Aysıla ŞİMSEK TEKELİ Merve ÜNAL Bengisu YILDIRIM Gamze PAKEN Dental Ölçülerin Dezenfeksiyonu Pınar YILDIZ İntraoral Dijital Ölçü Teknikleri Sevil Meral ŞAHMALI Münir DEMİREL Endodontik Tedavili Dişlerde Protetik Yaklaşımlar Mustafa Borga DÖNMEZ Sabit Protetik Restorasyonlarda Kullanılan Metal Alt Yapı Üretim Yöntemleri Mehmet BİÇER Server MUTLUAY ÜNAL Lityum Disilikat Cam Seramik Sistemleri: Son Güncellemeler Gonca DESTE Tam Seramik Restorasyonlarda Görülen Başarısızlıklar Işıl KARAOKUTAN İmplantüstü Protezlerde Yükleme Protokolleri Melahat Çelik Güven İmplant Destekli Protezlerde Okluzyon Damla GÜNEŞ ÜNLÜ Oklüzal Dikey Boyut Kayıplarının Protetik Açıdan Değerlendirilmesi Sadeq Mohammed Taqi FADHİL Emre MUMCU Hareketli Protezlerin Temizlenmesinde Kullanılan Materyal ve Yöntemler Zeynep YEŞİL DUYMUŞ Sebahat FINDIK AYDINER Maksillofasiyal Protezlerde Kullanılan Materyallere Genel Bakış ve Güncel Teknikler Almira Ada DİKEN TÜRKSAYAR