This study explores the controlled laser ablation and corresponding properties of silicon nanoparticles (Si NP) with potential applications in ultraviolet (UV) light sensing. The size distribution of Si NPs was manipulated by adjusting the laser scanning speed during laser ablation of a silicon target in a styrene solution. Characterization techniques, including transmission electron microscopy, Raman spectroscopy, and photoluminescence analysis, were employed to investigate the Si NP structural and photophysical properties. Si NP produced at a laser scanning speed of 3000 mm/s exhibited an average diameter of ~4 nm, polydispersity index of 0.811, and a hypsochromic shift in the Raman spectrum peak position. Under photoexcitation at 365 nm, these Si NPs emitted apparent white light, demonstrating their potential for optoelectronic applications. Photoluminescence analysis revealed biexponential decay behavior, suggesting multiple radiative recombination pathways within the nanoscale structure. Furthermore, a thin film containing Si NP was utilized as a passive filter for a 2nd generation CCD detector, expanding the functionality of the non-UV-sensitive detectors in optics, spectrometry, and sensor technologies.

The aim of this work was to investigate how ZnO tetrapod (ZnO-T) morphology, structure, and surface charge properties (i.e. Debye length) influence their UV sensing properties, shedding light on the underlying photoresponse mechanisms. ZnO-Ts were synthesized and centrifuged to obtain three different fractions with tuned morphology, which were characterized by scanning electron microscopy, transmission electron microscopy, and high-resolution transmission electron microscopy microscopies, x-ray diffraction analysis, Brunauer–Emmett–Teller measurements, FTIR and UV–vis spectroscopies. ZnO-T UV sensors were fabricated and tested comparing among ZnO-T fractions and commercial ZnO nanoparticles. ZnO-T photoresponse was mostly influenced by ZnO-T leg diameter, with the optimal value close to the double Debye length. We also demonstrated how fractionating ZnO-Ts for morphology optimization can increased the responsivity by 2 orders of magnitude. Moreover, ZnO-T showed 3 orders of magnitude higher responsivity compared to commercial ZnO nanopowder. These results are beneficial for the engineering of efficient UV sensors and contribute to a deeper understanding the overall mechanism governing UV photoresponse.

ZnO nanowires are often used for UV sensing, however in order to obtain high performance a complicated multistep process for preparation together with high measurement temperatures are used. In this work we demonstrate a facile one-step spray-coating method for the preparation of UV sensors based on ZnO tetrapod (ZnO-T) structure, demonstrating both high response (on/off) and fast rise-decay times at room temperature. Such UV sensors could be in principle deposited on any substrates; therefore this method could be used for flexible UV sensor preparation.