Klaudia Malisz

This study investigates the damage behavior and surface integrity of chitosan–nanohydroxyapatite (CS/nHAp) composite coatings, along with their corrosion resistance and wettability, which directly affect their biological performance in vivo. The coatings were deposited on Ti13Zr13Nb and stainless steel using electrophoretic deposition (EPD) at various voltages and deposition times. Surface topography, morphology, composition, and roughness were characterized using microscopic techniques, while wettability, corrosion resistance, and mechanical properties were assessed. Three-point bending tests were performed to determine coating behavior under mechanical deformation. Hydrophilic, homogeneous CS/nHAp coatings were successfully deposited without visible cracks on the surface. Coatings deposited at 10 V exhibited higher corrosion potentials compared to uncoated titanium alloy. Mechanical testing showed that coatings deposited at 10 V were significantly harder than those deposited at 20 V. The CS/nHAp20_5 coating exhibited moderate hardness (0.33 ± 0.06 GPa), the lowest Young’s modulus (12.7 ± 1.4 GPa), increased flexibility, and good adhesion, without delamination during bending tests. These results demonstrate that by modifying deposition parameters, it is possible to adjust the mechanical and protective properties of CS/nHAp coatings for potential application of the developed coating in vascular stents.

Microbial colonization in veterinary stents poses a significant and concerning issue in veterinary medicine. Over time, these pathogens, particularly bacteria, can colonize the stent surfaces, leading to various complications. Two weeks following the stent insertion procedure, the colonization becomes observable, with the aggressiveness of bacterial growth directly correlating with the duration of stent placement. Such microbial colonization can result in infections and inflammations, compromising the stent’s efficacy and, subsequently, the animal patient’s overall well-being. Managing and mitigating the impact of these pathogens on veterinary stents is a crucial challenge that veterinarians and researchers are actively addressing to ensure the successful treatment and recovery of their animal patients. In addition, irritation of the tissue in the form of an inserted stent can lead to overgrowth of granulation tissue, leading to the closure of the stent lumen, as is most often the case in the trachea. Such serious complications after stent placement require improvements in the procedures used to date. In this review, antibacterial or antibiofilm strategies for several stents used in veterinary medicine have been discussed based on the current literature and the perspectives have been drawn. Various coating strategies such as coating with hydrogel, antibiotic, or other antimicrobial agents have been reviewed.

Graphene is a two-dimensional nanomaterial composed of carbon atoms with sp² hybrid orbitals. Both graphene and graphene-based composite have gained broad interest among researchers because of their outstanding physiochemical, mechanical, and biological properties. Graphene production techniques are divided into top-down and bottom-up synthesis methods, of which chemical vapor deposition (CVD) is the most popular. The biomedical applications of graphene and its composite include its use in sensors, implantology, and gene and drug delivery. They can be used for tissue engineering, anticancer therapies, and as antimicrobial agents in implant application. The biocompatibility of graphene-based nanomaterials enables their use in the field of biomedicine. This article reviews the properties of graphene, the methods used to produce it, the challenges associated with its use, and the potential applications of this material in biomedicine, regenerative medicine, and drug delivery systems.

Diamond-like carbon (DLC) films are generally used in biomedical applications, mainly because of their tribological and chemical properties that prevent the release of substrate ions, extend the life cycle of the material, and promote cell growth. The unique properties of the coating depend on the ratio of the sp³/sp² phases, where the sp² phase provides coatings with a low coefficient of friction and good electrical conductivity, while the share of the sp³ phase determines the chemical inertness, high hardness, and resistance to tribological wear. DLC coatings are characterized by high hardness, low coefficient of friction, high corrosion resistance, and biocompatibility. These properties make them attractive as potential wear-resistant coatings in many compelling applications, including optical, mechanical, microelectronic, and biomedical applications. Another great advantage of DLC coatings is that they can be deposited at low temperatures on a variety of substrates and can thus be used to coat heat-sensitive materials, such as polymers. Coating deposition techniques are constantly being improved; techniques based on vacuum environment reactions are mainly used, such as physical vapor deposition (PVD) and chemical vapor deposition (CVD). This review summarizes the current knowledge and research regarding diamond-like carbon coatings.