Chrysa Charou

The goal of this paper is to investigate tungsten carbide (WC) as a reinforcement in the popular material extrusion (MEX) additive manufacturing (AM) procedure. The impressive characteristics of WC demonstrate its potential as a valuable additive for commonly used polymeric matrices in MEX 3D printing, offering reinforcement and stabilization properties. The mechanical properties of hybrid polymer/ceramic nanocomposites made up of various filler loadings (0–10 wt. %) of medical-grade polylactic acid (PLA) and WC were studied. The mechanical characteristics, structure, and thermomechanical properties of the resulting compounds were fully characterized following the respective standards. The fracture mechanisms were revealed with Scanning Electron Microscopy. Overall, a laborious effort was implemented with fifteen different tests to fully characterize the nanocomposites prepared. In comparison to the raw PLA material, the tensile strength of the 4.0 wt. % WC PLA/WC nanocomposite was improved by 42.5% and the flexural strength by 41.9%. In the microhardness test, a 120.4% improvement was achieved, justifying the properties of WC ceramic. According to these findings, PLA nanocomposites reach high-performance polymer specifications, expanding their potential use, especially in wear-related applications.

The development of bioactive, multi-functional, and cost-effective nanocomposite filaments for additive manufacturing (AM) is pivotal for the evolution of biomedical and healthcare sectors. Herein, an industrially scalable process is reported, to produce medical grade PA12/AgNP nanocomposites, through in-situ reactive melt-mixing, occurring within the filament extruder. Bactericidal elemental nanoparticles (Ag⁰) were formed by silver ions (Ag⁺) reducing from the Silver Nitrate (Ag₂NO₃) precursor, which was suitably added to the polymer melt. Polyvinyl Alcohol (PVA) was deployed in the compound melt, as a reducing macromolecular agent. The produced nanocomposite filaments were utilized to fabricate samples with Material Extrusion (MEX) AM. A total of sixteen (16) different tests were conducted on filaments and 3D-printed samples to assess their mechanical, rheological, thermal, and antibacterial characteristics, in accordance with international standards. The nanocomposites exhibited a significant mechanical reinforcement of up to 50% compared to PA12. Additionally, the Ag-based nanocomposites demonstrated remarkable antimicrobial behavior in the presence of Staphylococcus aureus (S. aureus) and Escherichia coli (E. coli) microbes.

In this study, innovative nanocomposite materials for material extrusion (MEX) 3D printing were developed using a polypropylene (PP) polymer with tungsten carbide (WC) nanopowder. The raw materials were converted into filaments using thermomechanical extrusion. The samples were then fabricated for testing according to the international standards. Extensive mechanical testing was performed on the 3D-printed specimens, including tensile, impact, flexural, and microhardness assessments. In addition, the impact of ceramic additive loading was examined. The thermal and stoichiometric characteristics of the nanocomposites were examined using thermogravimetric analysis, energy-dispersive X-ray spectroscopy, differential scanning calorimetry, and Raman spectroscopy. The 3D-printed shape, quality, and fracture process of the specimens were examined using scanning electron microscopy. The results showed that the filler significantly enhanced the mechanical characteristics of the matrix polymer without reducing its thermal stability or processability. Notably, the highest level of nanocomposite mechanical responsiveness was achieved through the inclusion of 6.0 and 8.0 wt. % fillers. The 10.0 wt. % loading nanocomposite showed significantly increased microhardness, indicating a possible high resistance to wear.

Both energy efficiency and robustness are popular demands for 3D-printed components nowadays. These opposing factors require compromises. This study examines the effects of seven general control variables on the energy demands and the compressive responses of polyamide (PA6) material extrusion (MEX) 3D printed samples. Nozzle Temperature, Layer Thickness, Orientation Angle, Raster Deposition Angle, Printing Speed, Bed Temperature, and Infill Density were studied. An L27 orthogonal array was compiled with five replicas. A total of 135 trials were conducted, following the ASTM D695-02a specifications. The stopwatch method was used to assess the construction time and energy usage. The compressive strength, toughness, and elasticity modulus were experimentally determined. The Taguchi technique ranks each control parameter’s impact on each response measure. The control parameter that had the greatest impact on both energy use and printing time was layer thickness. Additionally, the infill density had the greatest influence on the compressive strength. Quadratic regression model equations were formed for each of the response measures. The ideal compromise between mechanical strength and energy efficiency is now reported, with merit related to technological and economic benefits.

Herein, polytetrafluoroethylene (PTFE) is evaluated as a reinforcement agent in material extrusion (MEX) additive manufacturing (AM), aiming to develop nanocomposites with enhanced mechanical performance. Loadings up to 4.0 wt.% were introduced as fillers of polylactic acid (PLA) and polyamide 12 (PA12) matrices. Filaments for MEX AM were prepared to produce corresponding 3D-printed samples. For the thorough characterization of the nanocomposites, a series of standardized mechanical tests were followed, along with AFM, TGA, Raman spectroscopy, EDS, and SEM analyses. The results showed an improved mechanical response for filler concentrations between 2.0 and 3.0 wt.%. The enhancement for the PLA/PTFE 2.0 wt.% in the tensile strength reached 21.1% and the modulus of elasticity 25.5%; for the PA12/PTFE 3.0 wt.%, 34.1%, and 41.7%, respectively. For PLA/PTFE 2.0 wt.%, the enhancement in the flexural strength reached 57.6% and the modulus of elasticity 25.5%; for the PA12/PTFE 3.0 wt.%, 14.7%, and 17.2%, respectively. This research enables the ability to deploy PTFE as a reinforcement agent in the PA12 and PLA thermoplastic engineering polymers in the MEX AM process, expanding the potential applications.

The industrial demand for functional filaments made of bio-sourced, biocompatible, biodegradable, and/or recyclable polymers and composites for material extrusion (MEX) 3D printing is continuously growing. Polylactic acid (PLA), the most popular filament, combines such properties, yet its reinforcement with low-cost, inert, and/or recycled fillers remains challenging. Herein, glass in three different micro/nano-forms was the reinforcement agent in PLA. Three different experimental tiers were elaborated by producing composite filaments with glass in powder, beads, and flake forms in various loadings to optimize the concentrations. A thermomechanical process, i.e., melt filament extrusion, was exploited. The composites were evaluated for their thermal degradation stability and composition using thermogravimetric analysis and Raman. MEX 3D printing was used to produce tensile, flexural, impact, and microhardness specimens, to quantitatively evaluate their mechanical response. Field emission scanning electron microscopy evaluation and fractography were carried out to depict fracture patterns of the specimens after their tests. All three glass types induced impressive reinforcement effects (up to 60% in flexural loading), especially in the flake form. The impact of the additional process cost through glass fillers implementation was also assessed, indicating that such composites are cost-effective.

The current research aimed to examine the thermomechanical properties of new nanocomposites in additive manufacturing (AM). Material extrusion (MEX) 3D printing was utilized to evolve acrylonitrile butadiene styrene (ABS) nanocomposites with silicon nitride nano-inclusions. Regarding the mechanical and thermal response, the fabricated 3D-printed samples were subjected to a course of standard tests, in view to evaluate the influence of the Si₃N₄ nanofiller content in the polymer matrix. The morphology and fractography of the fabricated filaments and samples were examined using scanning electron microscopy and atomic force microscopy. Moreover, Raman and energy dispersive spectroscopy tests were accomplished to evaluate the composition of the matrix polymer and nanomaterials. Silicon nitride nanoparticles were proved to induce a significant mechanical reinforcement in comparison with the polymer matrix without any additives or fillers. The optimal mechanical response was depicted to the grade ABS/Si₃N₄ 4 wt. %. An impressive increase in flexural strength (30.3%) and flexural toughness (47.2%) was found. The results validate that these novel ABS nanocomposites with improved mechanical properties can be promising materials.