An asymmetric supercapacitor with extremely high energy and power densities has been developed by using the novel Fe₂O₃/VACNTs anode.

A high-performance ORR catalyst of Co supported on nitrogen and sulfur co-doped VACNTs was fabricated by cobalt sputtering and subsequent annealing in decomposition atmosphere of NH₄SCN.

(82−x)NbO_2.5–17.4LaO_1.5–xZrO₂(NLZ) (x = 7.5, 10, 12.5, 15, 17.5, and 20) bulk glasses codoped with Er³⁺/Yb³⁺ were successfully fabricated by aerodynamic levitation method for the first time. The structure, thermal stability, and luminescent properties of the samples were investigated systemically by XRD, differential scanning calorimetry, and upconversion spectra. Under 980 nm laser excitation, all samples exhibited green and red upconversion emissions centered at 531, 546, and 674 nm. Results showed that the sample with 15 mol% ZrO₂ obtained the most efficient upconversion luminescence and good thermal stability with the glass‐transition temperature as high as 743 °C. The effect of the addition of ZrO₂ on the structure behavior and the phonon density in the glass was investigated by Raman spectra, which are the key factors for the upconversion luminescence intensity.

The knowledge of thermophysical properties of active metals is critical to understand their metallurgical processes and further industrial applications. However, due to high reactivity and melt contamination from a crucible and gaseous environment, accurate values of the properties are hard to obtain using conventional methods such as the sessile-drop method. In the present study, a vacuum electrostatic levitator was used to circumvent these difficulties and enabled the noncontact determination of thermophysical properties of liquid cerium even in an undercooled state. The data of density, surface tension, and viscosity of molten cerium were reported, as well as their temperature dependence.