Graphene nanosheets (GNSs) have an extensive application in materials modification. In this study, the effects of graphene nanosheets on the wettability of Sn-20Bi lead-free solder on copper (Cu) substrate and the growth behavior of intermetallic compound (IMC) layers at Sn-20Bi-xGNS/Cu solder joints were investigated. The experimental results indicate that the wettability of Sn-20Bi solder firstly diminished and then increased by the addition of GNSs. Meanwhile, a prism-shaped and scallop-shaped Cu6Sn5 IMC layer was clearly observed at the interface of the solder/substrate system. Moreover, it was found that a small amount of GNS addition can significantly inhibit the growth of the IMC layer at the interface as well as refine the microstructure. Additionally, by nano-indentation apparatus, it can be concluded that the hardness and elastic module of IMCs show the same variation trend, which firstly decreased and then increased. Besides, to intuitively demonstrate the reliability of IMCs, the relationship between the hardness and elastic module was established, and the ratio of hardness/elastic module (H/E) was adopted to characterize the reliability of IMCs. The results show that when the addition of GNSs was 0.02 wt%, the value of H/E is the minimum and the solder joint has the highest reliability.

This study investigates the effect of aluminum (Al) on the microstructure, micro-hardness, and wettability of environmentally friendly Sn-20Bi-xAl (x = 0, 0.1, 0.3, 0.5 (wt.%)) solder alloys. Scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) analysis, and X-ray diffraction (XRD), were used to identify the microstructure morphology and composition. The spreading area and contact angle of the Sn-20Bi-xAl alloys on Cu substrates were used to measure the wettability of solder alloys. The results indicate that Al increased the hardness to a maximum value of ~27.1 HV for x = 0.5. When the content of Al was more than 0.3 wt.%, the hardness change value gradually flattened. From the spreading test results, Al reduced the wettability of solder alloys. When the content of Al was 0.1 wt.%, the change was slight. When more than 0.3 wt.%, the wettability of Sn-20Bi-xAl solder alloys sharply dropped. The corrosion resistance of Sn-20Bi-0.1Al alloy was the best, and the corrosion rate was at the lowest value at 0.092 mm/a due to the dense corrosion products.